Synthesis A Flexible Conductive Film of Poly 3,4-Ethylenedioxythiophene Polystyrene Sulfonate (PEDOT: PSS) Using Spray Pyrolysis Method Tarmidzi, Fadhil Muhammad; Sasongko, Setia Budi
International Journal of Renewable Energy Development Vol 7, No 2 (2018): July 2018
Publisher : Center of Biomass & Renewable Energy, Diponegoro University

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.14710/ijred.7.2.159-162

Abstract

Popularity of conducting polymers are become widely known and researches for practical application also has been done. In order to developed a continuous process for industrial scale,  we have proposed a spray pyrolysis method to synthesis a flexible conductive film of Poly(3,4-ethylenedioxythiophene) poly(styrene sulfonate) (PEDOT:PSS) on poly(ethylene terephthalate) (PET) and annealed at different temperatures and spray distances. The optimum condition that resulting a best morphology was anneal at 90oC and 20 cm distance with electrical conductivity 4.5 S/cm. It was found that annealing at temperature higher than 90oC will resulting a stress to a film and formed crack due to a different thermal expansion, while at the distance higher than 20 cm resulting a loss of PEDOT:PSS droplets. IR spectra shows that there is no any sign of PEDOT:PSS degradation even at 110oC. SEM analysis also show that the thickness is well distributed and there is no any sign of crack formedArticle History: Received February 24th 2017; Received in revised form May 16th 2018; Accepted May 20th 2018; Available onlineHow to Cite This Article: Tarmidzi, F.M. and Sasongko, S.B. (2018) Synthesis A Flexible Conductive Film of Poly 3,4-Ethylenedioxythiophene Polystyrene Sulfonate (PEDOT:PSS) Using Spray Pyrolysis Method. Int. Journal of Renewable Energy Development, 7(2), 159-162.https://doi.org/10.14710/ijred.7.2.159-162
Pengaruh Aktivator Asam Sulfat dan Natrium Klorida pada Karbon Aktif Batang Semu Pisang untuk Adsorpsi Fe Tarmidzi, Fadhil Muhammad; Putri, Maylina Anindita Sugiharti; Andriani, Anisa Novi; Alviany, Riza
Jurnal Rekayasa Bahan Alam dan Energi Berkelanjutan Vol 5, No 1 (2021)
Publisher : Fakultas Teknik, Universitas Brawijaya

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Batang semu pisang merupakan salah satu bahan alam kaya selulosa yang murah. Nilai batang semu pisang yang rendah dapat ditingkatkan menjadi material karbon aktif yang berkelanjutan dan ramah lingkungan. Karbon aktif batang pisang dapat digunakan untuk adosrpsi Fe dalam air baku. Sistem adsorpsi menjadi teknologi yang cocok untuk digunakan di daerah pedesaan yang mengandalkan air tanah. Oleh karena itu, penelitian ini bertujuan untuk mengembangkan sistem karbon aktif untuk adosrpsi Fe dari air tanah. Sintesis karbon aktif dilakukan dengan pencucian untuk menghilangkan getah dan komponen terlarut, pengeringan suhu 105oC selama 3 jam, karbonisasi suhu 400oC selama 30 menit, aktivasi asam menggunakan H2SO4, dan penetralan. Penelitian ini dilakukan untuk mempelajari pengaruh konsentrasi aktivator pada 0,3 M; 0,5 M; dan 0,7 M terhadap bilangan iodin dan kemampuan adosrpsi Fe. Konsentrasi Fe ditentukan dengan menggunakan spektroskopi adsorpsi atom (SSA). Hasil penelitian menunjukkan bahwa penggunaan aktivator 0,3 M H2SO4 memberikan hasil terbaik dengan bilangan iodin 58,23 mg/g dan Fe teradsorp sebanyak 80,85%.