Pemanfaatan serat alam kulit terap sebagai bahan kombinasi pembuatan winglet sepeda motor Rianto, Ari; Anjiu, Leo Dedy; Suhendra, Suhendra
TURBO [Tulisan Riset Berbasis Online] Vol 9, No 1 (2020): Jurnal TURBO
Publisher : Universitas Muhammadiyah Metro

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (349.286 KB) | DOI: 10.24127/trb.v9i1.1140

Abstract

The development of new natural fiber material as a composite reinforcing material needs to be continued. The use of natural fibers developed in this study was obtained from applied bark. The applied skin fiber is chosen as a composite reinforcing material because it has strong characteristics when pulled. This study was conducted to determine the impact strength of a combination of the arrangement of the composite layer of applied fiber and glass fiber with a polyester resin matrix in the manufacture of motorcycle winglets. The making of composite specimens was carried out by hand lay-up and pressing techniques. composite specimens tested consisted of composite A (100% fiberglass), composite B (100% applied fiber), composite C (fiberglass, applied fiber, fiberglass), and composite D (applied fiber, fiberglass, applied fiber). The treatment of the applied fiber was carried out by soaking 5% NaOH for 2 hours. Impact test specimens and procedures refer to the ASTM D256-00 standard. The results of the study obtained that the material recommended in the manufacture of motorcycle winglets is composite C, which is a combination of fiberglass, applied fiber, fiberglass. The results of the C composite impact strength testing were obtained at 2.6581 J / mm2. The impact strength of composite C increased by 79% compared to the impact strength of composite B using pure applied fiber (100% applied fiber). The large void tendency in natural fiber composites using the hand lay-up method reduces the impact strength so that fiberglass is more dominant as a determinant of the impact strength increase.Keywords : Applied fiber, impact test, winglet.
ANALISIS PENINGKATAN KUALITAS PROSES PENGEMASAN AIR MINUM DALAM KEMASAN “FOR3” 240 ML DENGAN MENGGUNAKAN PENDEKATAN METODE SIX SIGMA DAN FMEA (STUDI KASUS: PT. METEOR PERKASA, SINGKAWANG - KALBAR) Anjiu, Leo Dedy
Rekayasa Vol 4, No 2: Oktober 2011
Publisher : Universitas Trunojoyo Madura

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (351.448 KB) | DOI: 10.21107/rekayasa.v4i2.2333

Abstract

PT. Meteor Perkasa yang berlokasi di jalan Lirang Dusun Gunung Besi Kota Singkawang Provinsi Kalimantan Barat merupakan perusahaan yang bergerak pada bidang produksi Air Minum Dalam Kemasan (AMDK). Produk yang dihasilkan adalah produk merek “For3” dengan 3 jenis kemasan yaitu kemasan galon 19 liter, botol 1500 ml, botol 600 ml, botol 330 ml dan gelas 240 ml. Berdasarkan observasi awal, produk cacat banyak ditemukan pada kemasan AMDK “For3” 240 ml. Proses inspeksi dilakukan secara visual sebelum produk disusun ke dalam kardus. Pada proses ini ditemukan beberapa kriteria cacat yaitu cacat cup, cacat lid, cacat volume dan cacat kualitas produk. Untuk mengatasi permasalahan itu maka digunakan pendekatan DMAIC pada Six Sigma yang mampu mereduksi defect dan juga dengan metode FMEA yang diharapkan dapat mengidentifikasi penyebab masalah dan memberikan usulan perbaikan dalam peningkatan kualitas. Berdasarkan perhitungan dengan metode Six Sigma, telah terjadi peningkatan baik nilai DPMO dan Sigma Level setelah perbaikan. Untuk data variabel terjadi penurunan nilai DPMO dari 180.246 menjadi 175.423 dan terjadi peningkatan sigma level dari 2,41 menjadi 2,43. Sedangkan untuk data atribut terjadi penurunan nilai DPMO dari 5.983 menjadi 2.087 dan terjadi peningkatan sigma level dari 4,01 menjadi 4,36. Sedangkan analisis dengan menggunakan metode FMEA diperoleh bahwa nilai RPN mengalami penurunan setelah rekomendasi diterapkan. Hal ini dapat diketahui dari nilai RPN pada tahap control lebih kecil daripada RPN pada tahap Analyze, sehingga menunjukkan keberhasilan dari tindakan perbaikan yang telah dilakukan. Kata kunci: Peningkatan Kualitas, Six Sigma, FMEA AbstractPT. Meteor Mighty located in the hamlet Lirang Singkawang Iron Mountain West Kalimantan is a company engaged in the production of bottled water (mineral water). The resulting product is the product brand “for3” with 3 types of packaging, namely packaging gallon 19 liter, 1500 ml bottles, 600 ml bottles, bottles of 330 ml and 240 ml glass. Based on preliminary observations, defective products are found on the packaging of bottled drinking water “for3” 240 ml. Conducted a visual inspection process before the product is organized into boxes, the process discovered some defects are defects criteria cup, lid defects, defect volume and product quality defects. In order to solve the problem, we used the Six Sigma DMAIC approach which is able to reduce defects and FMEA methods are expected to identify the cause of the problem and proposes improvements in quality improvement. Based on calculations by the method of Six Sigma that there has been an increase in both the value of DPMO and Sigma Level after repair, to a decline in the value of the variable data DPMO of 180,246 to 175,423 and an increase in the sigma level of 2.41 to 2.43. As for the decline in the value of the attribute data from 5983 to 2087 DPMO and sigma level increased from 4.01 to 4.36. While the analysis obtained using the FMEA RPN values decreased after the recommendation is applied, it can be seen from the value of RPN in the Control phase is smaller than the NDP in the Analyze phase, indicating the success of remedial actions that have been performed. Key words: Quality improvements, Six Sigma, FMEA 
Kekuatan Mekanik Komposit Berpenguat Serat Kulit Terap Kontinu Sebagai Pengembangan Material Teknik Ramah Lingkungan Rianto, Ari; Anjiu, Leo Dedy
POSITRON Vol 8, No 1 (2018): May Edition
Publisher : Fakultas Matematika dan Ilmu Pengetahuan Alam, Univetsitas Tanjungpura

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1031.873 KB) | DOI: 10.26418/positron.v8i1.24029

Abstract

Telah dilakukan kajian eksperimental untuk mengetahui kekuatan tarik, kekuatan bending dan karakteristik perpatahan komposit serat kulit terap kontinu dengan perlakuan serat sebagai penguat komposit bermatriks resin polyester. Dalam penelitian ini, spesimen komposit dibuat dengan teknik hand lay-up dan pressing. Pembuatan spesimen komposit dengan penguat serat kulit terap bermatriks resin polyester dengan 3 lapisan serat terap dengan volume resin sebesar 70% sehingga resin yang digunakan sebanyak 168 g. Serat direndam selama 2 jam dalam larutan NaOH dengan konsentrasi yang bervariasi mulai dari 0%, 5%, 10%, 15%, 20%. Spesimen pengujian tarik dan bending mengacu pada standar ASTM D638-03 dan standar ASTM D 790-02. Hasil yang dicapai dari pengujian tarik yang dilakukan yaitu kekuatan tarik tertinggi pada variasi perlakuan NaOH 10 % terhadap serat terap dengan nilai sebesar 26,32 MPa meningkat 44% dari spesimen uji tanpa perlakuan NaOH dengan kekuatan tarik terendah sebesar 18,23 MPa. Nilai modulus elastisitas dan kekuatan bending tertinggi pada perlakuan perendaman dengan 15% NaOH dengan nilai berturut-turut sebesar 3,96 GPa dan 79,27 MPa. Bentuk patahan pada spesimen uji tanpa perlakuan NaOH menunjukkan banyak terjadi debonding dan pull-out dibandingkan patahan dengan perlakuan NaOH.