Article Per Year (5 Year)
p-Index From 2019 - 2024
0.61
P-Index
This Author published in this journals
All Journal EKUIVALEN - Pendidikan Matematika IJOG : Indonesian Journal on Geoscience Jurnal technoscientia Jurnal Penelitian Tanaman Industri Buletin Tanaman Tembakau, Serat & Minyak Industri BERITA BIOLOGI Journal of Geoscience, Engineering, Environment, and Technology Jurnal Ilmu dan Riset Akuntansi Metalurgi Pedagogiana - Jurnal Pendidikan Dasar JURNAL TEKNOLOGI TECHNOSCIENTIA
Sri Mulyaningsih
Balai Penelitian Tanaman Pemanis dan Serat
Agriculture, Biological Sciences & Forestry Biochemistry, Genetics & Molecular Biology Chemical Engineering, Chemistry & Bioengineering Computer Science & IT Decision Sciences, Operations Research & Management Earth & Planetary Sciences Economics, Econometrics & Finance Education Energy Engineering Environmental Science Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mathematics Mechanical Engineering Physics Other

Published : 24 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search
Journal : Metalurgi

 1 
PENGARUH KOMPOSISI LARUTAN TERHADAP KANDUNGAN Mo DALAM LAPISAN PADUAN Ni-Mo SECARA ELEKTROPLATING Mulyaningsih, Sri; Priyono, Budi
Metalurgi Vol 26, No 3 (2011): Metalurgi Vol. 26 No. 3 Desember 2011
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (383.081 KB) | DOI: 10.14203/metalurgi.v26i3.21

Abstract

Telah dilakuka n penelitian tentang pembuatan lapisan paduan Ni-Mo  yang akan digunakan sebagai lapisan bond coat untuk lapisan tahan temperatur tinggi (TBC). Penelitian dilakukan dengan menggunakan bahan dasar plat nikel 99% yang diroll dan dibentuk sampel berukuran 25 x 50 x 2 mm. Sampel kemudian diberi lapisan dengan  cara elektroplating  menggunakan  larutan  yang  terdiri dari NiSO4 , Na2MoO4 ,  C8H8O7. Komposisi larutan divarisikan menjadi 5 jenis larutan dengan perbandingan; I.  0,1 : 0,1: 0,1 mol, II. 0,075 : 0,125 : 0,1 mol, III. 0,050 : 0,100 ,0,1 mol, IV. 0,025 : 0,125: 0,1 moll dan V. 0,001 : 0,2 : 0,1 mol. Proses dilakukan pada suhu ruang dengan rapt arus 0,1 A/dm2. Dari hasil percobaan diperoleh bahwa larutan III menghasilkan lapisan dengan kadar Mo terbaik yaitu 21,19%. AbstractThere has been done the experiment about electro deposition Ni-Mo alloy as a bond coat layer for high temperature resistance coating, known as Thermal barrier coating (TBC). The sample is made from Nickel 99%. Roll process was done to thinning the samples and then cut the material into 25 x 50 x 2 mm shape. Electroplating process was done on the surface of materials by mixed NiSO4, Na2MoO4 and C8H8O7 for the solution. Electroplating process was carried out at 0,1-0,6 A/dm2 at room temperature. Composition of the solution was varied within I. 0,1 : 0,1: 0,1 mol, II. 0,075 : 0,125 : 0,1 mol, III. 0,050 : 0,100 , 0,1 mol, IV. 0,025 : 0,125: 0,1 moll and V. 0,001 : 0,2 : 0,1 mol. The best Mo content from the experiment is NiMo coating from solution III, it was 21,19 %.
Co-Authors . Djumali Alansa, Frando Ryan Ari Kusnaedi Arifin, Muhammad Nur Arisandy, Rydo Faisal B. Astuti Budi Hariyono Budi Priyono Busro, Djumali Darwin Alijasa Siregar Deny Juanda Puradimaja Devi, L R Devi, L R Dina Tania DJUMALI DJUMALI, DJUMALI Dwi Indah Purnamawati, Dwi Indah G. Hartono Heri Prabowo Heriyadi, Nur Widi Astanto Agus Tri Husadani, Y T Husadani, Y T I. Simon I. W. Prasetyanto IGAA. INDRAYANI, IGAA. Irawan, S N Irawan, S N Mohamad Faizal, Mohamad Muhammad Suyanto, Muhammad Nur Handayani Rahayu, Hanifah Aulia Sampurno Sampurno Sanjoto, Siwi Sanjoto, Siwi Suhartono Sutikno Bronto Tatawu, Ariel l Afrandi Teger Basuki Umboro, P A Umboro, P A Widayati, Wiludjeng Wijaksono, Shandi Hargian Wiwik Handayani Yahdi Zaim Yunengsih, Yuyun