Sintesis ZSM-5 dari Coal Fly Ash (CFA) dengan Sumber Silika Penambah yang Berasal dari Abu Sekam Padi: Pengaruh Rasio SiO2/Al2O3 Terhadap Kristalinitas Produk Azlia Metta; Simparmin Br Ginting; Hens Saputra
Jurnal Rekayasa Proses Vol 8, No 2 (2014)
Publisher : Departemen Teknik Kimia Fakultas Teknik Universitas Gadjah Mada

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (660.648 KB) | DOI: 10.22146/jrekpros.11374

Abstract

Coal Fly Ash and rice husk ash can be utilized by converting it into ZSM-5 synthetic zeolite. One of the influencing factors of ZSM-5 synthetis is ratio of SiO2/Al2O3. Synthesis of ZSM-5 was carried out in an autoclave at a temperature of 180°C with a variation of the ratio of SiO2/Al2O3, namely 20, 30, 40, 50 and 60 mol/mol during 24 hour crystallization using TPABr template. Characterization of ZSM-5 was conducted using X-ray Diffraction, Scanning Electron Microscopy, Adsorption-Desorption Analysis of Nitrogen and Acidity. The results showed that the ZSM-5 was formed in all the variations of SiO2/Al2O3 ratios with the highest percent crystallinity of 52.83%, at the ratio of 50 mol/mol. All products are still in accompany with the formation of side products such as Analsime and Silica Oxide. The ZSM-5 crystal product was in hexagonal shape. Results from Adsorption-Desorption Analysis of Nitrogen indicated that all products were mesoporous materials. Keywords: crystallinity, mesopore, ZSM-5, silica, rice husk, SiO2/Al2O3 ratio Limbah Coal Fly Ash dan abu sekam padi dapat dimanfaatkan dengan mengkonversi limbah menjadi zeolit sintesis ZSM-5. Salah satu faktor yang mempengaruhi sintesis ZSM-5 adalah rasio SiO2/Al2O3. Sintesis ZSM-5 dilakukan di dalam autoklaf pada suhu 180C dengan variasi rasio SiO2/Al2O3 yaitu 20, 30, 40, 50 dan 60 mol/mol selama waktu kristalisasi 24 jam menggunakan template TPABr. Karakterisasi ZSM-5 menggunakan metode Difraksi Sinar X, Scanning Electron Microscopy, Adsorpsi – Desorpsi Nitrogen dan Analisis Keasaman. Hasil penelitian menunjukkan bahwa ZSM-5 terbentuk pada semua variasi SiO2/Al2O3. Persen kristalinitas produk ZSM-5 sebesar 52,83%, ada pada rasio 50 mol/mol. Semua produk masih disertai terbentuknya produk samping seperti Analsime dan Silika Oksida. Kristal ZSM-5 yang dihasilkan berbentuk heksagonal. Hasil Analisis Adsorpsi-Desorpsi nitorgen mengindikasikan bahwa semua sampel adalah material mesopori. Kata kunci: kristalinitas, mesopori, ZSM-5, sekam, rasio SiO2/Al2O3
Sintesis ZSM-5 dari Coal Fly Ash (CFA) dengan Sumber Silika Penambah yang Berasal dari Abu Sekam Padi: Pengaruh Rasio SiO2/Al2O3 Terhadap Kristalinitas Produk Azlia Metta; Simparmin Br Ginting; Hens Saputra
Jurnal Rekayasa Proses Vol 8, No 2 (2014)
Publisher : Departemen Teknik Kimia Fakultas Teknik Universitas Gadjah Mada

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.22146/jrekpros.11374

Abstract

Coal Fly Ash and rice husk ash can be utilized by converting it into ZSM-5 synthetic zeolite. One of the influencing factors of ZSM-5 synthetis is ratio of SiO2/Al2O3. Synthesis of ZSM-5 was carried out in an autoclave at a temperature of 180°C with a variation of the ratio of SiO2/Al2O3, namely 20, 30, 40, 50 and 60 mol/mol during 24 hour crystallization using TPABr template. Characterization of ZSM-5 was conducted using X-ray Diffraction, Scanning Electron Microscopy, Adsorption-Desorption Analysis of Nitrogen and Acidity. The results showed that the ZSM-5 was formed in all the variations of SiO2/Al2O3 ratios with the highest percent crystallinity of 52.83%, at the ratio of 50 mol/mol. All products are still in accompany with the formation of side products such as Analsime and Silica Oxide. The ZSM-5 crystal product was in hexagonal shape. Results from Adsorption-Desorption Analysis of Nitrogen indicated that all products were mesoporous materials. Keywords: crystallinity, mesopore, ZSM-5, silica, rice husk, SiO2/Al2O3 ratio Limbah Coal Fly Ash dan abu sekam padi dapat dimanfaatkan dengan mengkonversi limbah menjadi zeolit sintesis ZSM-5. Salah satu faktor yang mempengaruhi sintesis ZSM-5 adalah rasio SiO2/Al2O3. Sintesis ZSM-5 dilakukan di dalam autoklaf pada suhu 180C dengan variasi rasio SiO2/Al2O3 yaitu 20, 30, 40, 50 dan 60 mol/mol selama waktu kristalisasi 24 jam menggunakan template TPABr. Karakterisasi ZSM-5 menggunakan metode Difraksi Sinar X, Scanning Electron Microscopy, Adsorpsi – Desorpsi Nitrogen dan Analisis Keasaman. Hasil penelitian menunjukkan bahwa ZSM-5 terbentuk pada semua variasi SiO2/Al2O3. Persen kristalinitas produk ZSM-5 sebesar 52,83%, ada pada rasio 50 mol/mol. Semua produk masih disertai terbentuknya produk samping seperti Analsime dan Silika Oksida. Kristal ZSM-5 yang dihasilkan berbentuk heksagonal. Hasil Analisis Adsorpsi-Desorpsi nitorgen mengindikasikan bahwa semua sampel adalah material mesopori. Kata kunci: kristalinitas, mesopori, ZSM-5, sekam, rasio SiO2/Al2O3