Article Per Year (5 Year)
p-Index From 2019 - 2024
0
P-Index
This Author published in this journals
All Journal Majalah Ilmiah Material, Komponen dan Konstruksi
Sutarjo .
Author
Civil Engineering, Building, Construction & Architecture Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering

Published : 6 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 6 Documents
Search

 1 
ANALISIS KEGAGALAN SHAFT POMPA SUBMERSIBLE PADA UNIT PENGEBORAN MINYAK BUMI = FAILURE ANALYSIS OF PUMP SHAFT SUBMERSIBLE ON OIL DRILLING UNIT Sunandrio, Hadi; ., Sutarjo
Majalah Ilmiah Material, Komponen dan Konstruksi Vol 14, No 1 (2014)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1930.778 KB)

Abstract

Vital component of a pump is the shaft, which serves to continue the torque of the driving during the operation and the seat of the impeller and other rotating parts.This research will be observed and taken action to find the cause of the damage that the sentence is not complete.The results showed that the main cause of damage to the pump shaft submersible because one shaft surfaces that are in the bearings rub against each other to generate heat, consequently between the shaft and the bearing sticking together, so the shaft is stopped suddenly resulting in rows experiencing shock loads (impact load) then the motor continues to rotate, resulting in shaft having torsional force. Because the area is an area that has a radius concentrated high voltage, then the broken shaft in the arearesulted in the remaining of word is not clear a broken pump shaft on oil drilling unit.Examinations and tests performed on the pump shaft, include: fraktografi and metallographic examination and hardness testing. Data from the results of examination and tests are then analyzed to determine the cause of the fracture on the pump shaft.Keywords : pump shaft, impact loads, torsional force, brokenAbstrak Komponen vital dari sebuah pompa adalah shaft, yang berfungsi untuk meneruskan momen puntir dari penggerak selama beroperasi dan tempat kedudukan impeller dan bagian-bagian yang berputar lainnya.Pada penelitian ini akan diamati dan diambil tindakan untuk mencari penyebab kerusakan yang mengakibatkan patahnya shaft pompa submersible pada unit pengeboran minyak bumi.Hasil penelitian menunjukkan bahwa penyebab utama kerusakan dari shaft pompa karena salah satu permukaan shaft yang berada di dalam bearing saling bergesekan hingga menimbulkan panas, akibatnya antara shaft dan bearing saling menempel, sehingga shaft terhenti secara tiba-tiba yang mengakibatkan shaf mengalami beban kejut (impact load) saat itu motor masih terus berputar, akibatnya shaft mengalami gaya puntir. Karena di daerah radius merupakan daerah yang mempunyai konsentrsi tegangan tinggi, maka shaft patah di daerah tersebut.Pemeriksaan dan pengujian yang dilakukan terhadap shaft pompa, meliputi : pemeriksaan fraktografi dan metalografi dan uji kekerasan. Data dari hasil pemeriksaan dan pengujian tersebut kemudian di analisa untuk mengetahui penyebab terjadinya patah pada shaft pompa tersebut.Kata kunci : shaft pompa, beban kejut, gaya puntir, patah
ANALISA KERUSAKAN PIPA PEMANAS AIR UNTUK UAP PEMBANGKIT LISTRIK = FAILURE ANALYSIS OF WATER HEATER PIPE FOR STEAM GENERATOR ., Sutarjo; Syahril, M.
Material Komponen dan Konstruksi Vol 14, No 2 (2014)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (553.449 KB)

Abstract

Heater’s pipes are used as a media for heating of fluids or changing of their ofphase from liquid to vapor/gas. Rupture of these pipes may cause all systems inthe production process stopand the high economic losses. This study aims toavoid the cases to accur in the future.Visual inspection, macrography, microstructure, hardness test and SEM-EDAXexamination were the methods applied in this study. It was known that the piperuptured atthe 6 o'clock area, the hardness value of which was identical to thematerial tensile strength (476 MPa), conforming to the standard specification andthe same indication was also indicated from the microstructure of the normalferrite-pearlite phase. At atemperature of about 390 C and traces of wall thinningin around 4:30 to 7:30, the pipes ruptured due to the thin walls could notwithstand the internal pressure of the pipe . The thinking occurred because thewater-level in the heater’s pipes was to low,resulting in cavitation of vaporbubbles on the inside surface of pipe wall.Keywords: Pipe, rupture, thin-wall, water-level, temperature, cavitation.AbstrakPipa heater digunakan sebagai media untuk memanaskan fluida atau untukmerubah fase dari cair menjadi uap/gas. Pecahnya pipa dapat menyebabkansemua sistim dalam proses produksi akan menjadi berhenti dan potensi kerugiansecara ekonomi tinggi. Penelitian ini bertujuan untuk menghindari kasuskerusakan yang serupa dimasa mendatang.Pemeriksaan visual, makrografi, struktur mikro, uji kekerasan dan pemeriksaanSEM dan EDAX merupakan metode yang diterapkan dalam penelitian ini.Diketahui bahwa pipa pecah pada area jam 6,nilai kekerasan yang identik dengankekuatan tarik material (476 MPa) masih di atas standar spesifikasi dan indikasiyang sama juga ditunjukkan dari struktur mikro yaitu fase ferit – pearlit normal.Dengan suhu sekitar 390 C dan jejak penipisan dinding di sekitar 4:30-7:30,sehingga pecahnya pipa karena dinding tipis tidak bisa menahan tekanan dalampipa dan penipisan terjadi disebabkan air tingkat di pemanas pipa terlalu rendah,sehingga mengakibatkan kavitasi gelembung uap pada permukaan dalam dindingpipa.Kata Kunci : Pipa, pecah, dinding tipis, tingkat-air, temperatur, kapitasi.
PENGARUH PERUBAHAN MIKROSTRUKTUR TERHADAP PERUBAHAN KEKERASAN RADIANT TUBE YANG TELAH BEROPERASI SEJAK 2003 Sari, Laili Novita; ., Sutarjo
Material Komponen dan Konstruksi Vol 16, No 1 (2016)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1230.98 KB) | DOI: 10.29122/mkk.v16i1.3289

Abstract

B2TKS - Sub- Analysis of Damage and residual life has done Remaining Life Assessment to the radiant tube on oil and gas companies from 2003 - 2016. In determining the RLA, it was used graph of the Era Technology where the determination is based on the microstructural changes while there are no literature or research which shows the hardness changing of material ASTM A 213 T5 which occurs during the aging process. Therefore it need to make formulation about the changes of spheriodizationto the chages of hardness of radiant tube material ASTM A 213 T5. By knowing a reasonable decrease in hardness to spheriodization, it was expected to detect the abnormal condition or damage earlier. Based on the examination of metallographic and hardness testing ,is was known that the reduction of hardness occur in proportion to the increase ofsperiodization percentage. In spheriodzation changing of Classification A, B, C the decrease of hardness below 0.7 HB / HB0 while classification D until the next classification,reduction of hardness above 0,7HB / HB0.AbstrakB2TKS – Sub Bidang Analisa Kerusakan dan umur sisa telah melakukan Remaining Life Assesment pada radiant tube pada perusahaan minyak dan gas bumi dari tahun 2003 – 2016. Dalam penentuan RLAdigunakan grafik dari Era Teknologi dimana penentuannya berdasarkan perubahan struktur mikro sedangkan untuk perubahan kekerasan material belum ada literatur atau penelitianyang menunjukkan tentang perubahan kekerasan pada material ASTM A 213 T5yang terjadi selama proses penuaan. Karena itu dilakukan perumusanperubahan kekerasan terhadap speriodisasi pada tube radiant material ASTM A 213 T5. Dengan mengetahui penurunan kekerasan yang wajar terhadap speriodisasi diharapkan akan mempermudah pendeteksian awal kondisi abnornal atau kerusakan. Berdasarkan pengamatan metalografi dan uji kekerasan diketahui bahwa penurunan kekerasan terjadi secara proporsional dengan peningkatan prosentase spriodisasi. Klasifikasi A, B, C penurunan kekerasan dibawah 0,7 HB/HB0 sedangkan klasifikasi D sampai berikutnya penurunan kekerasan diatas 0,7HB/HB0.Keywords: hardness, radiant tube, in situ metallography, ASTM A 213 T5
PENGARUH PERUBAHAN MIKROSTRUKTUR TERHADAP PERUBAHAN KEKERASAN RADIANT TUBE YANG TELAH BEROPERASI SEJAK 2003 Sari, Laili Novita; ., Sutarjo
Jurnal Material Komponen dan Konstruksi Vol. 16 No. 1 (2016)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1230.98 KB) | DOI: 10.29122/mkk.v16i1.3289

Abstract

B2TKS - Sub- Analysis of Damage and residual life has done Remaining Life Assessment to the radiant tube on oil and gas companies from 2003 - 2016. In determining the RLA, it was used graph of the Era Technology where the determination is based on the microstructural changes while there are no literature or research which shows the hardness changing of material ASTM A 213 T5 which occurs during the aging process. Therefore it need to make formulation about the changes of spheriodizationto the chages of hardness of radiant tube material ASTM A 213 T5. By knowing a reasonable decrease in hardness to spheriodization, it was expected to detect the abnormal condition or damage earlier. Based on the examination of metallographic and hardness testing ,is was known that the reduction of hardness occur in proportion to the increase ofsperiodization percentage. In spheriodzation changing of Classification A, B, C the decrease of hardness below 0.7 HB / HB0 while classification D until the next classification,reduction of hardness above 0,7HB / HB0.AbstrakB2TKS – Sub Bidang Analisa Kerusakan dan umur sisa telah melakukan Remaining Life Assesment pada radiant tube pada perusahaan minyak dan gas bumi dari tahun 2003 – 2016. Dalam penentuan RLAdigunakan grafik dari Era Teknologi dimana penentuannya berdasarkan perubahan struktur mikro sedangkan untuk perubahan kekerasan material belum ada literatur atau penelitianyang menunjukkan tentang perubahan kekerasan pada material ASTM A 213 T5yang terjadi selama proses penuaan. Karena itu dilakukan perumusanperubahan kekerasan terhadap speriodisasi pada tube radiant material ASTM A 213 T5. Dengan mengetahui penurunan kekerasan yang wajar terhadap speriodisasi diharapkan akan mempermudah pendeteksian awal kondisi abnornal atau kerusakan. Berdasarkan pengamatan metalografi dan uji kekerasan diketahui bahwa penurunan kekerasan terjadi secara proporsional dengan peningkatan prosentase spriodisasi. Klasifikasi A, B, C penurunan kekerasan dibawah 0,7 HB/HB0 sedangkan klasifikasi D sampai berikutnya penurunan kekerasan diatas 0,7HB/HB0.Keywords: hardness, radiant tube, in situ metallography, ASTM A 213 T5
ANALISA KERUSAKAN PIPA PEMANAS AIR UNTUK UAP PEMBANGKIT LISTRIK = FAILURE ANALYSIS OF WATER HEATER PIPE FOR STEAM GENERATOR ., Sutarjo; Syahril, M.
Material Komponen dan Konstruksi Vol 14, No 2 (2014)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (553.449 KB) | DOI: 10.29122/mkk.v14i2.1659

Abstract

Heater?s pipes are used as a media for heating of fluids or changing of their ofphase from liquid to vapor/gas. Rupture of these pipes may cause all systems inthe production process stopand the high economic losses. This study aims toavoid the cases to accur in the future.Visual inspection, macrography, microstructure, hardness test and SEM-EDAXexamination were the methods applied in this study. It was known that the piperuptured atthe 6 o'clock area, the hardness value of which was identical to thematerial tensile strength (476 MPa), conforming to the standard specification andthe same indication was also indicated from the microstructure of the normalferrite-pearlite phase. At atemperature of about 390 C and traces of wall thinningin around 4:30 to 7:30, the pipes ruptured due to the thin walls could notwithstand the internal pressure of the pipe . The thinking occurred because thewater-level in the heater?s pipes was to low,resulting in cavitation of vaporbubbles on the inside surface of pipe wall.Keywords: Pipe, rupture, thin-wall, water-level, temperature, cavitation.AbstrakPipa heater digunakan sebagai media untuk memanaskan fluida atau untukmerubah fase dari cair menjadi uap/gas. Pecahnya pipa dapat menyebabkansemua sistim dalam proses produksi akan menjadi berhenti dan potensi kerugiansecara ekonomi tinggi. Penelitian ini bertujuan untuk menghindari kasuskerusakan yang serupa dimasa mendatang.Pemeriksaan visual, makrografi, struktur mikro, uji kekerasan dan pemeriksaanSEM dan EDAX merupakan metode yang diterapkan dalam penelitian ini.Diketahui bahwa pipa pecah pada area jam 6,nilai kekerasan yang identik dengankekuatan tarik material (476 MPa) masih di atas standar spesifikasi dan indikasiyang sama juga ditunjukkan dari struktur mikro yaitu fase ferit ? pearlit normal.Dengan suhu sekitar 390 C dan jejak penipisan dinding di sekitar 4:30-7:30,sehingga pecahnya pipa karena dinding tipis tidak bisa menahan tekanan dalampipa dan penipisan terjadi disebabkan air tingkat di pemanas pipa terlalu rendah,sehingga mengakibatkan kavitasi gelembung uap pada permukaan dalam dindingpipa.Kata Kunci : Pipa, pecah, dinding tipis, tingkat-air, temperatur, kapitasi.
ANALISIS KEGAGALAN SHAFT POMPA SUBMERSIBLE PADA UNIT PENGEBORAN MINYAK BUMI = FAILURE ANALYSIS OF PUMP SHAFT SUBMERSIBLE ON OIL DRILLING UNIT Sunandrio, Hadi; ., Sutarjo
Jurnal Material Komponen dan Konstruksi Vol. 14 No. 1 (2014)
Publisher : Badan Pengkajian dan Penerapan Teknologi (BPPT)

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1930.778 KB) | DOI: 10.29122/mkk.v14i1.1653

Abstract

Vital component of a pump is the shaft, which serves to continue the torque of the driving during the operation and the seat of the impeller and other rotating parts.This research will be observed and taken action to find the cause of the damage that the sentence is not complete.The results showed that the main cause of damage to the pump shaft submersible because one shaft surfaces that are in the bearings rub against each other to generate heat, consequently between the shaft and the bearing sticking together, so the shaft is stopped suddenly resulting in rows experiencing shock loads (impact load) then the motor continues to rotate, resulting in shaft having torsional force. Because the area is an area that has a radius concentrated high voltage, then the broken shaft in the arearesulted in the remaining of word is not clear a broken pump shaft on oil drilling unit.Examinations and tests performed on the pump shaft, include: fraktografi and metallographic examination and hardness testing. Data from the results of examination and tests are then analyzed to determine the cause of the fracture on the pump shaft.Keywords : pump shaft, impact loads, torsional force, brokenAbstrak Komponen vital dari sebuah pompa adalah shaft, yang berfungsi untuk meneruskan momen puntir dari penggerak selama beroperasi dan tempat kedudukan impeller dan bagian-bagian yang berputar lainnya.Pada penelitian ini akan diamati dan diambil tindakan untuk mencari penyebab kerusakan yang mengakibatkan patahnya shaft pompa submersible pada unit pengeboran minyak bumi.Hasil penelitian menunjukkan bahwa penyebab utama kerusakan dari shaft pompa karena salah satu permukaan shaft yang berada di dalam bearing saling bergesekan hingga menimbulkan panas, akibatnya antara shaft dan bearing saling menempel, sehingga shaft terhenti secara tiba-tiba yang mengakibatkan shaf mengalami beban kejut (impact load) saat itu motor masih terus berputar, akibatnya shaft mengalami gaya puntir. Karena di daerah radius merupakan daerah yang mempunyai konsentrsi tegangan tinggi, maka shaft patah di daerah tersebut.Pemeriksaan dan pengujian yang dilakukan terhadap shaft pompa, meliputi : pemeriksaan fraktografi dan metalografi dan uji kekerasan. Data dari hasil pemeriksaan dan pengujian tersebut kemudian di analisa untuk mengetahui penyebab terjadinya patah pada shaft pompa tersebut.Kata kunci : shaft pompa, beban kejut, gaya puntir, patah