Astronomy Biochemistry, Genetics & Molecular Biology Chemical Engineering, Chemistry & Bioengineering Chemistry Civil Engineering, Building, Construction & Architecture Computer Science & IT Control & Systems Engineering Decision Sciences, Operations Research & Management Earth & Planetary Sciences Education Electrical & Electronics Engineering Energy Engineering Industrial & Manufacturing Engineering Library & Information Science Materials Science & Nanotechnology Mathematics Mechanical Engineering Physics Social Sciences Transportation

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Analysis of the Mechanical Properties of Teak Sawdust-Reinforced Composite Boards Affected by the Alkalization Process Reza Putra; Muhammad Muhammad; T Hafli; Nurul Islami; Muhammad Nugraha P; M Irsyad K
International Journal of Engineering, Science and Information Technology Vol 2, No 4 (2022)
Publisher : Master Program of Information Technology, Universitas Malikussaleh, Aceh Utara, Indonesia

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.52088/ijesty.v2i4.303

Abstract

The development of the teak wood processing industry is growing rapidly, especially in the Aceh area. Allows a lot of waste to be generated. This research was conducted by utilizing sawn wood waste into particle boards. To test the physical and mechanical properties of particleboard using a matrix of teak waste and SHCP 2668 WNC resin with a ratio of 60: 40, and variations in treatment (NaOH) 2,5, 5, and 7,5% in immersion for 2 hours. Then the particleboard is compressed using a hot press machine at a temperature of 150˚C for 20 minutes, and a pressure of 50 kg/cm2. Then tested according to SNI 03-2105-2006 standards, namely density, thickness expansion, moisture content, elasticity, and modulus of fracture. The results of the particle board test on the physical and mechanical properties test, namely the density yielded the best value for the 5% (NaOH) treatment with a value of 0.854 gr/cm3, the best water content test with 2.5% (NaOH) treatment with a value of 4.563 %, viscous development with treatment (NaOH) 5% with a value of 7.573%, the best elasticity test on treatment (NaOH) 2.5% with a value of 2.470 kgf/cm2, and the best fracture modulus test on treatment (NaOH) 7.5% with a value of 48.611 kgf/cm2 declared to meet the standard requirements of SNI 03-2105-2006. With alkaline treatment, particleboard gives a relatively good value compared to no treatment.
Co-Authors M Irsyad K Muhammad Muhammad Nurul Islami T Hafli