KARAKTERISASI ELEKTROLIT POLIMER OPTIMUM KITOSAN/PVA+KOH -, R.Putri; -, A.Maddu; -, Irzaman
Sistem Informasi Vol 1 No 2 (2011): Jurnal Photon
Publisher : Fakultas MIPA dan Kesehatan Universitas Muhammadiyah Riau

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (651.982 KB)

Abstract

The blend-based polymer electrolyte comprising of chitosan and polyvinyl alcohol (PVA) as host polymers and potassium hydroxide (KOH) 35% wt as the complexing salt was studied. Polymer electrolyte were obtained by the casting technique. FTIR, XRD, SEM and EDX studies have been made to investigate the structural, complexation in film morphology of the polymer electrolyte.
STUDI KONDUKTIVITAS ELEKTROLIT POLIMER KITOSAN/PVA+KOH -, R.Putri; -, A.Maddu; -, Irzaman
Sistem Informasi Vol 1 No 2 (2011): Jurnal Photon
Publisher : Fakultas MIPA dan Kesehatan Universitas Muhammadiyah Riau

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (626.062 KB)

Abstract

The blend-based polymer electrolyte consisting of chitosan and polyvinyl alcohol (PVA) as host polymers and potassium hydroxide (KOH) as the complexing salt was studied. Polymerelectrolyte were obtained by the casting technique. An attempt was also made to investigate the effect of TiO2 concentration in the chitosan/PVA+KOH polymer electrolyte. The best ionic conductivity values of 1,105 x 10-2 S cm-1 at room temperature were obtained for the sample containing 35%wt of KOH and 1,210 x 10-2 S cm-1 for the sample containing 50% wt TiO2. The polymer electrolyte with good ionic conductivity properties were characterized by thermal analysis (DSC). The glass transition temperature about 75.30 °C for the optimum Chitosan/PVA+KOH