Pengaruh Temperatur Austenisasi terhadap Struktur Mikro dan Nilai Kekerasan Material 14%Cr-3%Ni-2%Mo-2%C untuk Aplikasi Bola Gerus

Imaniar Romaeni (Unknown)
Posman Manurung (Universitas Lampung)
Fajar Nurjaman (LIPI)



Article Info

Publish Date
07 Jul 2017

Abstract

This study was conducted to determine the effect of heat treatment in the form of sub-critical, austenization, quenching and tempering the hardness values of the white cast iron material as consideration for testing wear resistance of local and foreign products as grinding balls. Samples was treated sub-critical at a temperature of 700°C with a hold time of 2 hours and continued with austenization temperature variation of 850, 950 and 1050°C with a hold time of each sample is 5 hours. The optimum hardness value was obtained at a temperature of 950°C austenization in the amount of 68.3 HRC and decreased at a temperature of 1050°C. It is because the solubility of carbon elements making up the matrix. Next will be tempering at a temperature of 250°C and holding time 2 hours hardness values decreased but the value of wear resistance is obtained even better ie grinding balls of 0.03 g/kg of product due to the combination of its constituent elements, namely chromium-molybdenum and nickel are high the presence of wear phenomena induced martensite.

Copyrights © 2017






Journal Info

Abbrev

jtaf

Publisher

Subject

Materials Science & Nanotechnology Physics

Description

Jurnal ini diterbitkan oleh Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Lampung sebagai sarana untuk mempublikasikan hasil penelitian, artikel review dari peneliti-peneliti di bidang fisika teori dan aplikasinya. Jurnal ini terbit dua kali setahun (Januari dan ...