<![CDATA[Abstract. Research on the effect of Pb doping is 0; 0.1; 0.2; 0.3 and 0.4 to the phase growth of the Bi-2212 Ca 1,10 superconducting material was carried out by the solid method at a calcination temperature of 800°C for 10 hours and sintering temperature of 830°C for 20 hours. The effect of Pb doping on the phase growth of superconducting material can be seen by volume fraction, impurity, and degree of orientation. The results showed that samples without doping Pb (Pb 0) had lower volume fraction values than samples with doping Pb (Pb 0.1-0.4). Addition of Pb doping (Pb 0.1-0.4) will increase the volume fraction. The highest volume fraction (Fv) in doping Pb 0.4 was 80.99%, whereas the lowest volume fraction on doping Pb 0.1 was 67.73%. Samples without doping Pb (Pb 0) had a lower orientation grade value than samples with doping Pb (Pb 0.1-0.4). The addition of Pb doping 0.1 and 0.4 has a higher orientation degree compared to Pb doping of 0.2 and 0.3. The sample with doping Pb 0,1 has the highest orientation degree value that is 24,87%. Based on the SEM results all the seals have shown layers arranged in a direction (oriented) with empty space between the slab (void) is relatively small.]]>
Copyrights © 2017