Reversibilitas Reaksi Elektrokimia pada Elektroda Superkapasitor Zeolit Berbasis Silika Sekam Padi yang Dikalsinasi pada Suhu 450, 550, dan 650℃

Fatia Ulfah (Unknown)
S Suprihatin (Unknown)
Posman Manurung (Unknown)



Article Info

Publish Date
17 Jan 2017

Abstract

Zeolite based silica rice husk has been prepared at temperature of 450, 550, and 650℃. This research was conducted to study the effect of calcination temperature in forming of crystalline phases and standard electron rate constant (k0). The zeolite K450 was formed quartz and bohmite phases, zeolite K550 and K650 was formed cristobalite, stishovite, gamma-alumina, and natrolite phases. Electrochemical reaction of zeolite K450, K550 and K650 are irreversible. Peak potential oxidation-reduction is between 240 mV and 390 mV. The higher value of calcination, the higher value of k0. The k0 value of zeolite K450, K550, K650 at scan rate of 1 V/s are 29,658 x 10-9; 36,398 x 10-9; 77,110 x 10-9 cm/s respectively. Natrolite phase of zeolite K550 and K650 have changed zeolite charge be netral. Based on these result, value k0 of zeolite K550 and K650 are going to be a reversible.

Copyrights © 2017






Journal Info

Abbrev

jtaf

Publisher

Subject

Materials Science & Nanotechnology Physics

Description

Jurnal ini diterbitkan oleh Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Lampung sebagai sarana untuk mempublikasikan hasil penelitian, artikel review dari peneliti-peneliti di bidang fisika teori dan aplikasinya. Jurnal ini terbit dua kali setahun (Januari dan ...