Nurqori Setiawati (Universitas lampung)
Posman Manurung (Universitas Lampung)
Simon Sembiring (Universitas lampung)



Article Info

Publish Date
01 Jul 2018

Abstract

Nanoparticle of silica from pumice rockhas been synthesizedby using extracted method of NaOH with varying of 2,5 Mand 3,5 M.The pumice was extracted using NaOH, silica titration usingH2SO4 and purification of silica using HCl. The solution was calcination at 700°C for 2 hours. The XRD result showed that diffraction pattern of amorphous silica. The EDS result confirmed the purity of silica for NaOH 3,5 M were 75,84%. Particle size from TEM result is(11,32 ± 0,922) nm for NaOH 3,5 M. The surface area for NaOH of 2,5 M and 3,5 M are 178,7 m2/g and186,2m2/g respectively.

Copyrights © 2018






Journal Info

Abbrev

jtaf

Publisher

Subject

Materials Science & Nanotechnology Physics

Description

Jurnal ini diterbitkan oleh Jurusan Fisika Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Lampung sebagai sarana untuk mempublikasikan hasil penelitian, artikel review dari peneliti-peneliti di bidang fisika teori dan aplikasinya. Jurnal ini terbit dua kali setahun (Januari dan ...