Sifat Mekanik Baja Karbon Rendah Akibat Variasi Bentuk Kampuh Las dan Mendapat Perlakuan Panas Annealing dan Normalizing

Nukman (Jurusan Teknik Mesin Fakultas Teknik Universitas Sriwijaya)



Article Info

Publish Date
01 Jul 2009

Abstract

Low carbon steel represent one of material which is generally used in a machine component. It has good formability and machineability, and also having the nature of able to good welding ability. Because welding can causing the happening of change metallurgi at metal, deformation and tension termal. To increase strength of extension welding that is through hot treatment by Annealing And Normalizing. The ultimated stress of specimen, highest owned by non-welding non-heat treatment (= 53,24 kgf/mm2 by e = 5,552%). The highest ultimated stress of welding specimen owned by double type V (X) weld - normalizing specimen ( = 52,85 kgf/mm2). This matter effect of level wide surface weld formed by double type V (X). The ultimate stress of nonwelding non-heat treatment specimen, highest tension is  = 11,7504 kgf/mm2. Bending test for the welding specimen, highest tension owned by spesimen Normalizing – Square type  (I) ( = 12,4032 kgf /mm2).

Copyrights © 2009






Journal Info

Abbrev

jrm

Publisher

Subject

Aerospace Engineering Automotive Engineering Control & Systems Engineering Energy Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering

Description

Jurnal Rekayasa Mesin (JRM) Jurusan Teknik Mesin Universitas Sriwijaya adalah sebuah jurnal blind peer-review yang didedikasikan untuk publikasi hasil penelitian yang berkualitas dalam bidang ilmu Teknik Mesin namun tak terbatas secara implisit. Semua publikasi di Jurnal Rekayasa Mesin ini bersifat ...