Article Per Year (5 Year)
p-Index From 2019 - 2024
0
P-Index
This Author published in this journals
All Journal PIN Pengelolaan Instalasi Nuklir Urania Jurnal Ilmiah Daur Bahan Bakar Nuklir
Usman Sudjadi
Pusat Teknologi Bahan Bakar Nuklir (PTBBN), BATAN Kawasan Puspiptek-Tangerang Selatan 15314, Banten
Energy Materials Science & Nanotechnology

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search
Journal : Urania Jurnal Ilmiah Daur Bahan Bakar Nuklir

 1 
PENGARUH NITROCARBURIZING DC-PLASMA TEMPERATUR (550-700)OC TERHADAP PERUBAHAN KEKERASAN PERMUKAAN DAN MIKROSTRUKTUR PADA BAHAN SUS 304 Usman Sudjadi
Urania : Jurnal Ilmiah Daur Bahan Bakar Nuklir Vol 16, No 4 (2010): Oktober 2010
Publisher : website

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (1493.595 KB) | DOI: 10.17146/urania.2010.16.4.2422

Abstract

ABSTRAK Pengaruh Nitrocarburizing  DC-Plasma Temperatur (550-700)oC Terhadap Perubahan Kekerasan Permukaan Dan MikroStruktur Pada Bahan SUS 304 Beberapa samples telah di nitrocarburizing pada temperatur (550 – 700) 0C selama 1 jam.  Hasilnya menunjukkan bahwa, pada sample awal kekerasan bahan SUS 304 adalah 260,718 Kgf/mm2, setelah di nitrocarburizing pada temperatur 700 0C selama 1 jam, kekerasannya menjadi 279,88 Kgf/mm2, sedangkan kedalaman maximum atom-atom nitrogen dan carbon yang terdifusi kedalam bahan SUS 304 ialah 3,4 micrometer.  Pengamatan mikrostruktur menunjukkan bahwa pada sample yang telah di nitrocarburizing pada T = 700 0C (t= 1 jam) terlihat jelas adanya lapisan atom-atom N dan C di dalam bahan SUS 304.  Pada sample awal terdapat matrix γ-phase, δ-ferrite, dan twinning transformation. Pada samples yang di nitrocarburizing pada T > 5500C mempunyai matrix γ-phase, δ-ferrite, σ-phase, carbide dan twinning transformation. Kata kunci : Nitrocarburizing, DC plasma, SUS 304, kekerasan, dan mikrostruktur.   ABSTRACT Influence of nitrocarburizing DC Plasma to hardness and microstructure change on SUS 304 material apparatus.  Some samples were nitrocarburized at temperature (550-700) 0C for 1 hour. The results shows that the hardness untreated sample of SUS 304 material was 260,718 Kgf/mm2, after the sample nitrocarburized at temperature 700 0C for 1 hour, the hardness increasing to be 279,88 Kgf/mm2, furthermore maximum depth of carbon and nitrogen atoms that difused in SUS 304 material was 3,4 micrometer.  Microstructure observation shows that the sample after nitrocarburized at temperature 700 0C for 1 hour to be seen very clear that there are layer of N and C atoms in SUS304 material.  Un-treated sample has matrixes γ-phase, δ-ferrite, and twinning transformation. Samples that nitrocarburized at T > 5500C have matrixes γ-phase, δ-ferrite, σ-phase, carbide, and twinning transformation. Keywords : Nitrocarburizing, DC plasma, SUS304, hardness,and  microstructure.
Co-Authors Martoyo . Nusin Samosir