XRD Analysis of Li4Ti5O12 with Post Heat Treatment for Lithium-ion Capacitor (LIC) Applications

Syahrul Humaidi (Unknown)

Article Info

Publish Date
28 Feb 2022

Abstract

Characterization of XRD-analysis on Li4Ti5O12 with post heat treatment for applications Lithium-ion Capacitor (LIC) has been conducted. The powder method was used in the analysis, whereas the samples were prepared using the sol-gel method. The anode material Li4Ti5O12 precursor was sintered at 850°C for 4 hours and followed by heat-treatment at 600oC for 3 hours. Characterization of structural (XRD analysis) was applied to determine the formation of Li4Ti5O12 phase. The results of the characterization were formed Lithium titanate (Li4Ti5O12) and rutile phase (TiO2) with crystallite size on LTO I of 82.52 nm and LTO II of 92.07 nm. Overall, post heat treatment of anode Li4Ti5O12 succeeded in improving the quality and electrochemical performance for Lithium-ion Capacitor (LIC) application.

Copyrights © 2022




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Journal of Technomaterial Physics
Website

Abbrev

JoTP

Publisher

TALENTA PUBLISHER

Subject

Astronomy Civil Engineering, Building, Construction & Architecture Control & Systems Engineering Earth & Planetary Sciences Electrical & Electronics Engineering Energy Materials Science & Nanotechnology Physics

Description

Journal of Technomaterial Physics (JoTP) is a peer-review national journal that is published twice a year, in February and August. JoTP provides an open access policy for the writer and free publication charge. Due to its open access policy, JoTP serves online publication and a fast review process. ...