A New Synthesized Microalloys Steel ODS of High Amplitude Ultrasonically Irradiation

Silalahi, Marzuki (Unknown)
Wicaksana, Hanif Abdurrahman (Unknown)
Aziz, Ferhat (Unknown)
Ahda, Syahfandi (Unknown)
Iskandar, Mohamad Riza (Unknown)

Article Info

Publish Date
03 Dec 2019

Abstract

Micropowders of oxide-dispersion-strengthened (ODS) steel have been synthesized using the ultrasonic irradiation method with variations in amplitude. The ultrasonic irradiation process is performed for 50 h at a frequency of 20 kHz with 40%, 50%, and 60% amplitudes in toluene solution. The formation of Fe-Cr microalloys in the preparation of Fe- 15Cr-0.5Y2O3 powder was analyzed using SEM-EDS, X-ray diffraction (XRD), and TEM-EDS. The percentage of Fe- Cr phase mass fraction of ODS steel micropowder formed during ultrasonic irradiation with 40%:50%:60% amplitude was 12.2%:34.1%:22.1%, with 25.67:77.02:38.51 nm crystallite size. The crystallite size at 50% amplitude was the largest, and the diffusion process of Fe-Cr-Y2O3 microparticles was most dominant at 50% amplitude. The Fe and Cr phases are still present when the ODS particles successfully dispersed in the main particle.

Copyrights © 2019




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Makara Journal of Technology
Website

Abbrev

publication:mjt

Publisher

Universitas Indonesia

Subject

Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Electrical & Electronics Engineering Engineering Materials Science & Nanotechnology Mechanical Engineering

Description

MAKARA Journal of Technology is a peer-reviewed multidisciplinary journal committed to the advancement of scholarly knowledge and research findings of the several branches of Engineering and Technology. The Journal publishes new results, original articles, reviews, and research notes whose content ...