<![CDATA[This study aimed to evaluate the physical and mechanical properties of cross-laminated timber (CLT) characteristics from mangium (Acacia mangium) and puspa (Schima wallichii) woods and their combination using polyurethane (PU 1.2) adhesives. The manufacture of CLT began with basic adhesive characterization and thermo-mechanical analysis. Wood material’s physical and chemical properties were also tested with its response to the PU 1.2 wettability. The CLT (100 ´ 30 ´ 3.60) cm3 was manufactured with 160 g/m2 glue spread at a pressure of 0.80 MPa for 200 minutes. The CLT panels were characterized refers to the JAS 3079 standard. The results show that PU 1.2 had a gelatination time of 182.1 minutes at 25°C, was able to form urethane groups, and experienced an increase in storage modulus at 35°C. Mangium and puspa woods have different physical and chemical properties, but they interact similarly with PU 1.2 wettability. Puspa CLT panel has a higher density than mangium but lower dimensional stability. The bending mechanical properties of hybrid puspa-mangium-puspa CLT were able to match puspa CLT and have one sample of shear strength that met the JAS 3079 standard in both grain directions. Therefore, hybrid puspa-mangium-puspa CLT has the potential to be developed to improve its dimensional stability and mechanical properties. Keywords: Acacia mangium, cross-laminated timber, layer combination, polyurethane adhesive, Schima wallichii]]>
Copyrights © 2023