Pembentukan Titanium Nitrida (TiN) dengan Proses Nitriding pada Titanium Murni Menggunakan Plasma Densitas Tinggi

Windajanti, Josephine Maria (Unknown)
Santjojo, Dionysius Joseph Djoko Herry (Unknown)
Abdurrouf, Abdurrouf (Unknown)

Article Info

Publish Date
15 Aug 2017

Abstract

Pure titanium has been widely utilized in industry but its products suffered from low wear and erosion resistance. The plasma nitriding was selected as a tool to harden the pure titanium products but typically high temperature processing was required to attain high hardness. In the present study, high density plasma nitriding system was applied to make low temperature plasma nitriding at 723 K (or 450°C) for 14.4 ks (or 4 hours).  The average measured hardness reached to 624 HV.  This high hardness of plasma-nitrided pure titanium at low temperature was attributed to formation of fine TiN precipitates and nitrogen solid solution into vacancy sites in the HCP crystalline structure of titanium.

Copyrights © 2017




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Full PDF
776.563 KB
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Rekayasa Mesin
Website

Abbrev

rm

Publisher

Universitas Brawijaya

Subject

Mechanical Engineering

Description

Rekayasa Mesin is published by Mechanical Engineering Department, Faculty of Engineering, Brawijaya, Malang-East Java-Indonesia. Rekayasa Mesin is an open-access peer reviewed journal that mediates the dissemination of academicians, researchers, and practitioners in mechanical engineering. Rekayasa ...