Article Per Year (5 Year)
p-Index From 2019 - 2024
0.23
P-Index
This Author published in this journals
All Journal Indonesian Journal of Computing, Engineering, and Design
Ika O Suryani
Department of Mechanical Engineering, Faculty of Engineering and Technology, Sampoerna University
Arts Chemical Engineering, Chemistry & Bioengineering Computer Science & IT Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering

Published : 1 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search

 1 
Dynamic Contact Angle and Corrosion Test Measurements on Cu and CuO-Stearic Acid Modifications on Steel Surfaces Iwan Setiawan; Satria Robi Trisnanto; Ika O Suryani
Indonesian Journal of Computing, Engineering and Design (IJoCED) Vol 2 No 1 (2020): IJoCED
Publisher : Faculty of Engineering and Technology, Sampoerna University

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.35806/ijoced.v2i1.103

Abstract

In this study, a copper (Cu) coated steel surface’s dynamic contact angle and corrosion rate was compared to the bare steel and stearic acid modified surfaces. Various steps of surface treatment have been performed including electrodeposition of Cu, CuO formation from H2O2 immersion with stearic acid modification to obtain dynamic contact angle and the corrosion rate data. The Cu-coated steel’s dynamic contact angle was increased as it implied the surface after Cu treatment was more hydrophilic than the bare steel, with sliding angle and contact angle hysteresis of 54.9o ± 2.39o and 39.5o ± 1.91o, respectively. However, corrosion test measurements by using a mass loss method to quantify the corrosion rate showed that Cu-coated steel and stearic acid-modified Cu-O coated steel had no remarkable difference in corrosion rate. It was found that the Cu-coated steel and stearic acid-modified Cu-O coated steel had corrosion rate eight times slower than the bare surface.