<![CDATA[This research study examines the mechanical properties and morphology of epoxy-pineapple fiber leaves komposit as mass fraction with random fiber orientation. The purpose of this study was to determine the effect of pineapple leaf fiber on mechanical properties and morphology of composites. Composit with best structure of morphology is a composite with a mass of 0.7 g pineapple leaf fiber, it is concluded from SEM image which shows that the interface between matrix and aggregate is good. This indicates that the composite with a mass of pineapple leaf fibers has the highest flexural bending strength (flexural strength) compared to composites with a mass of 1.2 g and 1.7 g. This result is supported by the results of composites bending test using Testometric M500-25CT tool. Composites with a mass of 0.7 g pineapple leaf fibers, which is the highest one, is 5.74 MPa.Penelitian ini mengkaji tentang Studi Sifat Mekanik Dan Morfologi Komposit Serat Daun Nanas-Epoxy Ditinjau Dari Fraksi Massa Dengan Orientasi Serat Acak. Tujuan dari penelitian ini untuk mengetahui pengaruh penambahan serat daun nanas terhadap sifat mekanik dan morfologi komposit. Struktur morfologi komposit yang paling baik adalah komposit dengan massa serat daun nanas 0,7 g, hal ini diketahui dari citra SEM yang menunjukkan interface antar matriks dan agregat yang baik. Hal ini menandakan bahwa komposit dengan massa serat daun nanas memiliki kuat lentur lentur (Flexural Strength) tertinggi dibandingkan komposit dengan massa 1,2 g dan 1,7 g. Pernyataan ini didukung dari hasil uji lentur komposit dengan menggunakan alat Testometric M500-25CT. Komposit dengan massa serat daun nanas 0,7 g memiliki kuat lentur tertinggi yaitu 5,74 MPa.Kata Kunci: epoxy, komposit, serat daun nanas, kekuatan lentur]]>
Copyrights © 2015