Pengaruh temperatur terhadap struktur mikro dan sifat mekanik dalam proses fussion brazing Ni-Hard 4 dengan S45C menggunakan CuZn 35 sebagai logam pengisi.

Ari Siswanto (Politeknik Manufaktur Negeri Bandung (POLMAN))
W. Purwadi (Unknown)

Article Info

Publish Date
01 Apr 2020

Abstract

This research was conducted on white cast iron (Ni-Hard 4) and medium carbon steel (S45C) cast iron materials using a thin brass plate (CuZn 35) 0.3 mm as filler metal by heating at temperatures of 850 to 1050 0C for 120 minutes with a pressure of 2 Mpa in the muffle furnace. The effect of temperature on the microstructure was observed using an optical microscope and scanning electron microscopy equipped with energy dispersive X-ray system (EDS) to determine the chemical composition that occurred between the three meterial layers. The thickness of the interface layer increases with increasing holding temperature. The highest shear strength (79.86 Mpa) was obtained at a temperature of 950 0C.

Copyrights © 2020




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Full PDF
1040.799 KB
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Dinamika Teknik Mesin
Website

Abbrev

DTM

Publisher

Universitas Mataram

Subject

Automotive Engineering Energy Engineering Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering Physics

Description

The Dinamika Teknik Mesin: Jurnal Keilmuan dan Terapan Teknik Mesin is aimed to desiminating and sharing the scientific research results, simulations, and computation to reseachers, students, and practitioners around the world. It is a peer-reviewed academic journal which publishes originally ...