<![CDATA[Abstract.Edible film is a thin layer to protect food which it can be consumed. One of the main components to make edible film is starch, which could be derived from taro tubers. Taro tubers contain high starch content about 70-80% which consists of 5.55% of amylose and 74.45% of amylopectin with yield reach to 28.7%. However, the weakness of starch-based edible film are low resistance to water and low barrier properties to water vapor. One of the recommended hydrophobic biopolymers to improve the film characteristics of starch as well having antimicrobial activity is chitosan. The objectives of this research are to know the interaction and influence of starch concentration from taro tuber and concentration of chitosan on physical and mechanical character of edible film, including thickness, density, transparency, tensile, elongation and water vapor transmission eate (WVTR). The best treatment from first objective will apply on dodol (food made by glutinous rice) substituted by seaweed to know the effect of its application on dodol shelf life (texture analysis, weight loss and microbiology). Therefore this research was conducted in 2 stages and 2 experimental design methods. The first stage was the process of making edible film using Randomized Block Design method and the second stage was the application of edible film using Random Design Complete method. The results of physical and mechanical analysis of edible film based on its effect on the storage of dodol showed that the best treatment was obtained of P3K3 treatment (6% of Taro starch: 3% of Chitosan), P3K1 (6% of Taro starch: 1% of Chitosan) and P3K2 (6% Taro starch: 2% of Chitosan). The application of 3 types of edible films based on the best treatment of dodol substitute of seaweed has significant effects on the value of weight loss, texture and total plate count during the storage period. Effectiveness of edible film in inhibiting damage to dodol was obtained of P3K3 treatment (6% of Taro starch: 3% of Chitosan) with WVTR value equal to 0.189 g / cm2 hour, 0.170 N / mm2 of tensile strength, 0.088% of elongation, 0.160 mm of thickness, 0.151 of density and 0.000 mm-1of transparency.]]>
Copyrights © 2019