Effects of Calsium Carbonat on Hardness and Wear Behaviour of Brass-Epoxy Brake Lining Pad.

Fajar Nugroho (Sekolah Tinggi Teknologi Adisutjipto)

Article Info

Publish Date
10 Dec 2019

Abstract

Brake lining pad is important in driving safety. It must be able to stop the vehicle as quickly as possible. Calcium carbonate is The purpose of this study was to identify the effect of calcium carbonate to the brake brass-epoxy lining pad. Calcium carbonate meet have good physical properties, such as having low porosity and fine particles while brass has a good heat conductor and is corrosion resistant so it is resistant to heat. The tests carried out on brake pads include wear and hardness tests. The results showed that the optimal wear rate in a dry state (40% calcium carbonate-20% brass-40% epoxy) was 0.0352 mm²/kg. While the wear rate in wet conditions (20% calcium carbonate-40% brass-40% epoxy) was 0.0396 mm²/kg. The hardness brake lining pad (20% calcium carbonate - 40% brass -40% epoxy) was  176.44 kg/mm².

Copyrights © 2019




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Conference SENATIK STT Adisutjipto Yogyakarta
Website

Abbrev

senatik

Publisher

Institut Teknologi Dirgantara Adisutjipto

Subject

Aerospace Engineering Computer Science & IT Electrical & Electronics Engineering Industrial & Manufacturing Engineering Mechanical Engineering

Description

SENATIK merupakan jurnal proceeding seminar nasional teknologi informasi dan kedirgantaraan yang dikelola Pusat Penelitian,dan Pengabdian kepada Masyarakat (P3M) Sekolah Tinggi Teknologi Adisutjipto Yogyakarta. Jurnal ini diterbitkan dalam jangka waktu setahun sekali, dalam bentuk off line/ buku ...