Growth of CrSi2 Nanostructures Using CrCl2 Powder on Si Substrates

Li, Wen (Unknown)
Erchao, Meng (Unknown)
Matsushita, Tomoji (Unknown)
Oda, Shingo (Unknown)
Ishikawa, Daisuke (Unknown)
Nakane, Kaito (Unknown)
Tatsuoka, Hirokazu (Unknown)

Article Info

Publish Date
01 Apr 2013

Abstract

Chromium disilicide (CrSi2) nanostructures were grown by the exposure of Si (111) substrates to CrCl2 vapor in an argon gas flow at atmospheric pressure without using any metal catalyst. Dependence of the growth condition on the structural property was investigated. Hexagonal-shaped CrSi2 microrods were grown at 750 °C with 0.05 g of CrCl2. As the quantity of CrCl2 increased to 0.1 g, the bundle of CrSi2 nanowires with microrods and web-liked CrSi2 nanostructure with turning angles were grown at 750 °C and 700 °C, respectively. The preliminary discussion on the growth mechanism of CrSi2 micro- and nanostructures was carried out.

Copyrights © 2013




Citation Download
RIS
EndNote, Reference Manager, ProCite
BibTex
Latex, Jabref
Original Source
Download Original
Google Scholar
Check in Google Scholar
Journal Info
Makara Journal of Technology
Website

Abbrev

publication:mjt

Publisher

Universitas Indonesia

Subject

Chemical Engineering, Chemistry & Bioengineering Civil Engineering, Building, Construction & Architecture Electrical & Electronics Engineering Engineering Materials Science & Nanotechnology Mechanical Engineering

Description

MAKARA Journal of Technology is a peer-reviewed multidisciplinary journal committed to the advancement of scholarly knowledge and research findings of the several branches of Engineering and Technology. The Journal publishes new results, original articles, reviews, and research notes whose content ...