Pengaruh Proses Equal Channel Angular Pressing Terhadap Sifat Mekanik Aluminium Silikon Dengan Suhu Anil 300°C

Doni Eka Phutra.D (Jurusan Teknik Mesin, Fakultas Teknologi Industri, Institut Teknologi Medan Jl. Gedung Arca No. 52, Medan)
Yulfitra Yulfitra (Jurusan Teknik Mesin, Fakultas Teknologi Industri, Institut Teknologi Medan Jl. Gedung Arca No. 52, Medan)



Article Info

Publish Date
30 Sep 2018

Abstract

The aim of this study to study the effect of the Equal Channel Angular Pressing process the mechanical properties of aluminum silicon with annealing temperature of 300 ° C. An aluminum silicon rod with a length of 40 mm and a width of 9.5 mm in diameter is passed to the ECAP mold with a mold flow angle of 120 °. Material hardness and microstructure of materials before and after the ECAP process are examined and compared. The results showed that after the ECAP process, the hardness of aluminum silicon in the longitudinal section increased and was fairly evenly distributed, ie, at annealing time of 10 minutes the hardness value was 54.30 BHN, at 15 minutes resistance the hardness increased to 55.08 BHN and 25 minutes the hardness value rose to 55.69 BHN, as well as the microstructure showed that the longer the time annealed, the finer the grains on silicon aluminum.

Copyrights © 2018






Journal Info

Abbrev

RMME

Publisher

Subject

Aerospace Engineering Control & Systems Engineering Electrical & Electronics Engineering Energy Engineering

Description

Jurnal Rekayasa Material, Manufaktur & Energi, yang diterbitkan oleh Fakultas Teknik, Program Studi Teknik Mesin, Universitas Muhammadiyah Sumatera Utara (UMSU), Medan, Sumatera Utara, Indonesia, Jurnal Rekayasa Material, Manufaktur & Energi menerima artikel ilmiah hasil-hasil penelitian, dan ...