PENGARUH PENAMBAHAN Mg DAN Sr TERHADAP KEKERASAN KOMPOSIT ADC12/nano-Al2O3 DENGAN METODE STIR CASTING Ahmad Al Kautsar; Salahuddin Junus; Aris Zainul Muttaqina
STATOR: Jurnal Ilmiah Mahasiswa Teknik Mesin Vol 1 No 1 (2018): JURNAL STATOR
Publisher : STATOR: Jurnal Ilmiah Mahasiswa Teknik Mesin

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Metal matrix composites generally use Aluminum (Al) as its matrix because of its low density, high processing, and high ductility. Ductility is an important factor that must be possessed on the metal matrix composite because the amplifier used is rigid and brittle. Alumina (Al2O3) is used as a reinforcing particle in a metal matrix composite because it has good thermal stability and hardness as well as a high Young modulus. Aluminum-silicon alloys (Al-Si) are excellent alloys of good melting, which have a good surface, without brittleness, and are excellent for cast alloys. The addition of magnesium (Mg) resulted in a modified rate of silicone eutectic for Al-Si-Mg, with enhanced magnesium (Mg) levels, increased alloy tensile strength but a decreasing percent elongation value. Strontium (Sr) is a common element used to modify eutectic and Si-shaped phases of rough acicular into finer and rounded fibrous forms. A metal matrix composite with a nano-sized Al2O3 particle amplifier can be fabricated using stir casting method with the addition of Mg as a Al2O3 wetting agent. Test results of the addition of Mg, Sr, and nano-Al2O3 to the highest hardness of ADC12 / nano-Al2O3 composites were found in ADC12-8Mg-0.03Sr / 2.5nano-Al2O3 variation at 78.92 HRB. Keywords : Composite Al/nano-Al2O3, alumina, magnesium, strontium, stir casting, hardness