Pengaruh Substrat Terhadap Kekerasan Lapisan NiCoCrAlY Yang Terdeposisi Dengan Teknik HVOF[Effect of Different Substrate on Hardness Properties of NiCoCrAlY Coatings Deposited by HVOF Technique] Desiati, Resetiana Dwi; Sugiarti, Eni; Junianto, Endro; Martides, Erie; Prawara, Budi
Metalurgi Vol 32, No 2 (2017): Metalurgi Vol. 32 No. 2 Agustus 2017
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

Micro structure and micro hardness characterizations have been done on NiCoCrAl coating deposited on different substrate, i..e, carbon steel, nickel chrome and hastealloy. NiCoCrAlY coating was deposited by high velocity oxy fuel (HVOF) thermal spraying technique. Characterization and measurents were applied on all cross section of the coating surfaces. Micro structural analysis was characterized by optical microscope with 40x magnification. Moreover, micro hardness tester was utilized to measure the hardness of the sample with 300 gf for 13 second. The hardness data was measured by calculating the average of 3 position of hardness measurement on substrate before coating, after coating and NiCoCrAl coating layer. According to micro structural analysis, it reveald that the thickness of NiCoCrAlYcoating layer was about 370.76 mm, 92 mm, dan 115.73 on carbon steel, nickel chrome and hastealloy substrate, respectively. Surface morfology showed that the coated layer was not flat and porous structure or void on the coated layer. The porosity of the coated layer might effect the mechanical properties of the sample where high procentase of porosity might reduce the hardness of the sample. The hardness of NiCoCrAlY coating was about 349.95, 315.60 and 311.30 HV for carbon steel, nickel chrome and hastealloy substrate, respectively. The distance from interface between coating layer and substrate might effect hardness measurement. More closer to interface could decrease hardness value and it might caused by interdiffusion of coating elements. Thus would be effect to its mechanical properties.AbstrakTelah dilakukan karakterisasi strukturmikro dan kekerasan mikro pada lapisan NiCoCrAlY yang dideposisikan di atas substrat yang berbeda yaitu baja karbon, nikel krom dan hastealloy. Lapisan NiCoCrAlY dideposisikan menggunakan teknik penyemprotan HVOF (high velocity oxy fuel). Proses karakterisasi dan pengukuran dilakukan pada seluruh lapisan dengan irisan melintang. Karakterisasi strukturmikro diamati dengan menggunakan mikroskop optik dengan perbesaran 40x. Selanjutnya untuk pengukuran kekerasan menggunakan kekerasan mikro dengan beban 300 gf selama 13 detik. Data pengujian kekerasan diperoleh dengan mengukur nilai rata-rata dari 3 posisi uji kekerasan pada masing-masing bagian substrat sebelum dilapisi, setelah dilapisi dan lapisan NiCoCrAlY. Berdasarkan hasil karakterisasi strukturmikro diketahui bahwa lapisan NiCoCrAlY berhasil terdeposisi dengan ketebalan 370,76 mm, 92 mm, dan 115,73 mm masing-masing di atas substrat baja karbon, nikel krom dan hastealloy. Morfologi permukaan lapisan menunjukkan bahwa lapisan yang terdeposisi tidak begitu rata dan masih tampak adanya pori atau lubang di area lapisan NiCoCrAlY yang terbentuk. Porositas dari lapisan sangat berpengaruh pada sifat mekanik, semakin tinggi persentase porositas lapisan maka kekerasan akan menurun. Nilai kekerasan lapisan NiCoCrAlY pada substrat baja karbon adalah sebesar 349,95 HV, nikel krom sebesar 315,60 HV dan hastealloy sebesar 311,30 HV. Jarak dengan interface mempengaruhi pengukuran kekerasan. Semakin dekat dengan interface akan semakin menurun nilai kekerasaannya. Hal ini dipengaruhi oleh daerah interdifusi elemen pelapis sehingga mempengaruhi kekuatan mekaniknya.

Analisa Ukuran Partikel Serbuk Komposit NiCrAl dengan Penambahan Reaktif Elemen untuk Aplikasi Lapisan Tahan Panas Desiati, Resetiana Dwi; Sugiarti, Eni; Ramandhany, Safitry
Metalurgi Vol 33, No 1 (2018): Metalurgi Vol. 33 No. 1 April 2018
Publisher : Pusat Penelitian Metalurgi dan Material - LIPI

Dalam makalah ini dibahas mengenai ukuran sampel serbuk NiCrAl yang ditambahkan reaktif elemen yitrium (Y), silikon (Si), hafnium (Hf), dan zirconium (Zr) menjadi paduan NiCrAlY, NiCrAlSi, NiCrAlYSi, NiCrAlHf, NiCrAlZr dengan proses milling menggunakan ball mill selama 36 jam dengan kecepatan milling 25 Hz atau 1500 rpm dan perbandingan antara serbuk dengan ball mill adalah 1:2. Scanning electron microscopy (SEM) digunakan untuk mengkarakterisasi sampel serbuk yang bertujuan untuk mengetahui morfologi sampel seperti bentuk dan ukuran partikel. Gambar digital dari hasil karakterisasi SEM diolah menggunakan software ImageJ untuk mengetahui ukuran partikelnya dan hasilnya pengukurannya dibandingkan dengan data hasil karakterisasi menggunakan Particle Size Analizer (PSA). Berdasarkan hasil analisa dapat diketahui bahwa pengolahan gambar dijital SEM menggunakan ImageJ memiliki keakuratan kurang lebih sebesar 80%. Hal ini disebabkan dari bentuk sampel powder yang tidak homogen dan sebarannya yang tidak merata. Selain itu pula dapat diketahui juga bahwa sampel serbuk paduan NiCrAl, NiCrAlY, NiCrAlSi, NiCrAlYSi, NiCrAlHf, NiCrAlZr setelah pemilingan selama 36 jam mengalami perbesaran ukuran dari kondisi awal atau 0 jam yang disebabkan selama proses pemilingan mengalami aglomerasi dan coldwelding.

PENGARUH MODEL PEMBELAJARAN INQUIRY BERBASIS METODE PICTORIAL RIDDLE TERHADAP KEMAMPUAN BERKOMUNIKASI ILMIAH SISWA SMP Sugiarti, Eni; Susanto, Hadi; Khanafiyah, Siti
UPEJ Unnes Physics Education Journal Vol 4 No 3 (2015)
Publisher : UPEJ Unnes Physics Education Journal

Penelitian ini bertujuan untuk mengetahui pengaruh penerapan model pembelajaran inquiry berbasis metode pictorial riddle terhadap peningkatan pemahaman konsep dan kemampuan berkomunikasi ilmiah siswa SMP. Metode penelitian yang digunakan adalah metode eksperimen semu dengan desain one group pretest posttest. Teknik pengumpulan data yang digunakan dalam penelitian ini yaitu teknik dokumentasi, tes dan teknik observasi. Dari hasil uji gain didapatkan pemahaman konsep siswa meningkat dengan faktor gain sebesar 0,56 (sedang) dan kemampuan berkomunikasi ilmiah siswa meningkat dengan faktor gain sebesar 0,56 (sedang). Dari uji korelasi product moment didapatkan bahwa penerapan model pembelajaran inquiry berbasis metode pictorial riddle berpengaruh terhadap peningkatan pemahaman konsep dengan kriteria sedang dan berpengaruh terhadap peningkatan kemampuan berkomunikasi ilmiah siswa dengan kriteria kuat. Berdasarkan hasil tersebut dapat disimpulkan bawa model pembelajan inquiry berbasis metode pictorial riddle berpengaruh positif terhadap peningkatan pemahaman konsep dan kemampuan berkomunikasi ilmiah siswa SMP. The purpose of this research is to know the influence implementation of inquiry learning model with pictorial riddle method on increase the understanding concepts and scientific communication skill of junior high school students. The method used is quasi experimental with one group pretest and posttest design. Data collection method used in this research are documentation, test and observation. From the obtained gain test result shown that understanding concepts of students increased by a gain factor of 0,56 (medium) and scientific communication skill of students increased by a factor gain of 0,56 (medium). From the obtained product moment corelation test result shown that the implementation of inquiry learning model with pictorial riddle method influence on increasing of understanding concepts of students with medium criteria and influence on increasing of scientific communication skill of students with strong criteria. Based on the result above, it can be concluded that the implementation of inquiry learning model with pictorial riddle method gives positive influence to increase the understanding concepts and scientific communication skill of junior high school students.

Peningkatan Keterampilan Menulis Narasi melalui Media Jejaring Sosial Facebook Sugiarti, Eni
Journal of Language Learning and Research (JOLLAR) Vol 2 No 2 (2018)
Publisher : Department of Indonesian Language Education, Graduate School, University of Muhammadiyah Prof. DR. HAMKA

Show Abstract | Download Original | Original Source | Check in Google Scholar | Full PDF (768.136 KB)

Tujuan dalam penelitian ini adalah meningkatkan keterampilan menulis narasi siswa kelas IXA MTs Negeri 14 Jakarta melalui media jejaring sosial facebook. Metode penelitian ini adalah penelitian tindakan yang berlangsung 2 siklus. Siklus 1 dimulai dari perencanaan, pelaksanaan, evaluasi, dan refleksi. Siklus kedua memberikan kegiatan tambahan sebagai perbaikan perlakuan berdasarkan hasil refleksi siklus pertama. Hasil tes awal (pretes) kemampuan menulis narasi siswa rata-rata 63.4. Hasil tes akhir siklus I nilai rata-rata siswa meningkat dari 63,4 menjadi 68, dari 36 siswa siklus l hanya 11 siswa yang berhasil mencapai skor 70. Tes akhir siklus II lebih meningkat lagi dengan nilai rata-rata siswa 74,2. Seluruh subjek penelitian sudah memenuhi Kriteria Ketuntasan Minimum (KKM) yaitu 70. Dengan demikian, media jejaring sosial facebook dapat digunakan untuk meningkatkan hasil belajar menulis narasi siswa Kelas IXA MTs Negeri 14 Jakarta Tahun Pelajaran 2015/2016.

PENGARUH PH LARUTAN ELEKTROLIT TERHADAP TEBAL LAPISAN ELEKTROPLATING NIKEL PADA BAJA ST 37 Andinata, Febryan; Destyorini, Fredina; Sugiarti, Eni; Munasir, Munasir; Zaini T., Kemas A.
Jurnal Penelitian Fisika dan Aplikasinya (JPFA) Vol 2, No 2 (2012)
Publisher : Universitas Negeri Surabaya

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.26740/jpfa.v2n2.p48-52

Penelitian ini menggunakan metode eksperimen. Obyek eksperimen pada penelitian ini adalah plat baja karbon rendah (Baja ST 37) berbentuk plat persegi dengan dimensi p x l x t. Penelitian ini melalui beberapa tahapan yaitu, persiapan eksperimen dan pelaksanaan eksperimen. Persiapan eksperimen meliputi persiapan benda kerja, pembersihan benda kerja, serta pengukuran keasaman. Dalam penelitian ini masing-masing terdapat 7 kombinasi perlakuan pH pencelupan yaitu pH 3.02, 3.23, 3.40, 3.62, 3.82, 4.02, 4.20. Analisis data dalam penelitian ini menggunakan analisis Visual. Hasil didapat disimpulkan bahwa ada perbedaan massa hasil pelapisan nikel akibat larutan elektrolit dengan variasi pH pada bahan baja karbon rendah dengan taraf signifikasi sebesar 95%. Proses pelapisan nikel dengan menggunakan metode electroplating untuk bahan baja karbon rendah sebaiknya dilakukan pada pH yang memiliki tingkat keasaman pH 3.00 pada proses lapis nikel.

PENGARUH pH LARUTAN ELEKTROLIT TERHADAP TEBAL LAPISAN ELEKTROPLATING NIKEL PADA BAJA ST 37 Andinata, Febryan; Destyorini, Fredina; Sugiarti, Eni; Munasir, Munasir; Zaini T., Kemas A.
Jurnal Penelitian Fisika dan Aplikasinya (JPFA) Vol 2, No 2 (2012)
Publisher : Universitas Negeri Surabaya

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.26740/jpfa.v2n2.p48-52

Penelitian ini menggunakan metode eksperimen. Obyek eksperimen pada penelitian ini adalah plat baja karbon rendah (Baja ST 37) berbentuk plat persegi dengan dimensi p x l x t. Penelitian ini melalui beberapa tahapan yaitu, persiapan eksperimen dan pelaksanaan eksperimen. Persiapan eksperimen meliputi persiapan benda kerja, pembersihan benda kerja, serta pengukuran keasaman. Dalam penelitian ini masing-masing terdapat 7 kombinasi perlakuan pH pencelupan yaitu pH 3.02, 3.23, 3.40, 3.62, 3.82, 4.02, 4.20. Analisis data dalam penelitian ini menggunakan analisis Visual. Hasil didapat disimpulkan bahwa ada perbedaan massa hasil pelapisan nikel akibat larutan elektrolit dengan variasi pH pada bahan baja karbon rendah dengan taraf signifikasi sebesar 95%. Proses pelapisan nikel dengan menggunakan metode electroplating untuk bahan baja karbon rendah sebaiknya dilakukan pada pH yang memiliki tingkat keasaman pH 3.00 pada proses lapis nikel.

Title

Found 6 Documents
Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title Search

Found 6 Documents Search

Abstract

Abstract

Abstract

Abstract

Abstract

Abstract

Title

Found 6 Documents
Search