Article Per Year (5 Year)
p-Index From 2019 - 2024
0.444
P-Index
This Author published in this journals
All Journal JOURNAL OF MECHANICAL ENGINEERING, MANUFACTURES, MATERIALS AND ENERGY Journal of Physics: Theories and Applications
Wanatchaporn Namhongsa
Sakon Nakhon Rajabhat University
Education Energy Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering Physics

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Fabrication and Performance Analysis of AZO and MCCO as Thin Film-Thermoelectric Generator Materials Elysa Nensy Irawan; Fahrur Aslami; Aldo Mahendra Putra; Somporn Thaowankaew; Wanatchaporn Namhongsa; Athorn Vora-Ud; Kunchit Singsoog; Tosawat Seetawan4; Melania Suweni Muntini
JOURNAL OF MECHANICAL ENGINEERING MANUFACTURES MATERIALS AND ENERGY Vol. 6 No. 2 (2022): Edisi Desember 2022
Publisher : Universitas Medan Area

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31289/jmemme.v6i2.7317

Abstract

The purpose of this research was to determine the performance of AZO and MCCO materials as constituents of the thin film-thermoelectric generator module. The method used for fabrication is DC Magnetron Sputtering. The electrode material used is Ag and the substrate used is SiO2 glass. The arrangement of the thin film used for the fabrication of the thermoelectric module is P-N-P-N-P-N-P-N-P-N (5 couples of p-n junctions). Based on the test results, the thickness of the thin film type N is 74.72 nm and type P is 90.34 nm. At the highest test temperature (300 oC), the AZO Seebeck coefficient value is -108 µV/K while the MCCO Seebeck coefficient value is 350 µV/K, and the AZO electrical resistivity value is 0.07 Ω.m while the MCCO electrical resistivity value is 0.36 Ω.m. The highest temperature difference given in the test of the AZO and MCCO thin film thermoelectric module is 1.538 °C and the thermoelectric module can produce a voltage of 1,842 ± 0.047 mV, a Seebeck coefficient of 4 µV/K, and an efficiency of 0.44%. Based on this research, it can be concluded that the performance of AZO and MCCO thin film-thermoelectric modules will have better performance at temperatures around 300 - 350 °C.
Fabrication of p-type (MCCO) thin film using DC magnetron sputtering as a preparator for thermoelectric module Elysa Nensy Irawan; Fahrur Aslami; Muhammad Matthew Janotama; Aldo Mahendra Putra; Melania Suweni Muntini; Somporn Thaowankaew; Wanatchaporn Namhongsa; Athorn Vora-Ud; Kunchit Singsoog; Tosawat Seetawan
Journal of Physics: Theories and Applications Vol 7, No 1 (2023): Journal of Physics: Theories and Applications
Publisher : Universitas Sebelas Maret

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20961/jphystheor-appl.v7i1.66951

Abstract

Based on existing research, thermoelectric efficiency can be improved through material selection. In this study, the material used is CaCO₃ doped with Mn and Co₂O₃ to form CaCo3.5Mn0.5O9 material as a p-type thermoelectric material. The substrate used is glass. The stages in this research are material synthesis, sputtering process using DC Magnetron Sputtering machine to form thin films, and testing. The synthesis process includes grinding, calcination, and sintering. Grinding is done using a Ball Mill machine with a rotation speed of 250 rpm for 5 hours. Furthermore, the calcination step was carried out by heating the sample into a furnace at a temperature of 800°C for 10 hours. Then the sintering process was carried out at a temperature of 850°C for 12 hours. After the synthesis process is complete, enter the sputtering process using a DC Magnetron Sputtering machine for approximately 10 minutes. The gas used in this research is Argon (Ar). After the sputtering process was carried out, several tests appeared, such as the XRD test to determine the type of crystal, the ZEM-3 test to determine the Seebeck coefficient and resistivity, the thickness of the thin film formed, and the power factor test to determine the maximum voltage and power generated by the module formed. Several power factor test results were obtained, consisting of 107 μW/mK² at 100°C, 108 μW/mK² at 200°C, and 332 μW/mK² at 300°C and a thickness of 90.34 nm.