Article Per Year (5 Year)
p-Index From 2019 - 2024
0.817
P-Index
This Author published in this journals
All Journal Rotasi Jurnal Pendidikan Teknik Mesin Infotekmesin Journal of Applied Mechanical Technology (JAMET) Indonesian Journal of Community Empowerment
Leo Van Gunawan, Leo Van
Pendidikan Teknik Mesin, Universitas Negeri Semarang
Aerospace Engineering Agriculture, Biological Sciences & Forestry Humanities Automotive Engineering Computer Science & IT Education Electrical & Electronics Engineering Environmental Science Industrial & Manufacturing Engineering Materials Science & Nanotechnology Mechanical Engineering Public Health

Published : 6 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search
Journal : Infotekmesin

 1 
Analisis Pengaruh Variasi Suhu Tempering Pada Sifat Mekanik Baja ASTM A36 Setelah Pengelasan SMAW Menggunakan Elektroda E 7016 Gunawan, Leo Van; Satya Andika, Puger; Endramawan, Tito; Haris, Emin; Sukardi, Casiman; Satria Jati, Unggul
Infotekmesin Vol 15 No 1 (2024): Infotekmesin: Januari, 2024
Publisher : P3M Politeknik Negeri Cilacap

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.35970/infotekmesin.v15i1.2144

Abstract

ASTM A36 is a type of structural metal that can be applied for various purposes such as making gears, bridge structures and ship buildings. After welding, ASTM A36 steel will produce residual stress. Residual stress in the welded metal is caused not balanced temperature distribution. The method for eliminating residual stress is tempering. Tempering is used to reduce residual stresses, increase the ductility and toughness of metals. This research aims to analyze the effect of variations in tempering temperature on the mechanical properties of ASTM A36 steel after SMAW welding using E7016 electrodes. The tensile strength test on the specimen showed the highest increase due to the tempering effect of 537,880 MPa at a temperature of 200°C. This is proven by the reduction in material hardness of 165.07 VHN at a tempering temperature of 200°C when compared to the hardness of the raw material. The growth of ferrite grains in the material structure shows that the ASTM A36 material is increasingly ductile after tempering. The results of research on the effect of variations in tempering temperature on the mechanical properties of ASTM A36 can be used as an alternative way to increase ductility after the welding process