Article Per Year (5 Year)
p-Index From 2019 - 2024
0.408
P-Index
This Author published in this journals
All Journal JTT (Jurnal Teknologi Terapan) Jurnal Altifani Penelitian dan Pengabdian kepada Masyarakat
Yanti Pasmawati
Universitas Bina Darma
Religion Humanities Computer Science & IT Education Languange, Linguistic, Communication & Media Nursing Public Health Social Sciences

Published : 2 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 2 Documents
Search

 1 
Pemanfaatan Teknologi Berbasis Internet of Things (IOT) Pada Budidaya Ikan: Automatic Fish Feeder Sunda Ariana; Nina Paramithya; Yanti Pasmawati; Fero Triando; Muhamad Ariandi; Noer Fadzri Perdana Dinata; Andries Anwar; Sulaiman Helmi; Dewi Sartika
Jurnal Altifani Penelitian dan Pengabdian kepada Masyarakat Vol. 3 No. 4 (2023): Juli 2023 - Jurnal Altifani Penelitian dan Pengabdian kepada Masyarakat
Publisher : Indonesian Scientific Journal

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.59395/altifani.v3i4.463

Abstract

Pemberian pakan ikan merupakan aktivitas paling penting dan harus dilakukan secara konsisten baik jumlah maupun waktu pemberian pakan. Jika tidak dilakukan secara konsisten maka akan mempengaruhi pertumbuhan ikan dan tentunya berdampak pada hasil panen. Untuk mengatasi permasalahan tersebut, maka tujuan kegiatan pengabdian masyarakat ini memanfaatkan teknologi berbasis internet of things (IOT) dalam merancang alat pakan ikan secara otomatis (automatic fish feeder). Metode kegiatan yang dilakukan adalah pelatihan dan pendampingan. Mitra adalah Desa Gelebek Dalam dan Korem 44/Gapo. Komponen dan alat yang disiapkan antara lain power supply, real time clock (RTC), sensor ultrasonik, arduino uno, mega+wifi r3 atmega 2560+esp 8266, lcd 20x4, buzzer, kipas, lcd keypad shield, switch/saklar, panel box, motor servo. Analisis hasil menggunakan metode performance dan kuesioner. Hasil uji coba menunjukkan bahwa alat automatic fish feeder memiliki kinerja atau performa yang baik. Terbukti dari semua sistem dan proses dapat dijalankan dengan baik dan sesuai dengan fungsi maupun manfaat yang diharapkan. Selain itu, alat ini juga dapat membantu pembudidaya mengontrol pemberian pakan ikan secara jarak jauh. Sehingga, peternak ikan tidak mengalami keterlambatan dalam pemberian pakan dan juga early warning sebelum persediaan pakan habis. Selain kebergunaan, pelatihan ini juga memberikan pengetahuan tentang perawatan alat serta mampu meningkatkan kemampuan dan pengetahuan tentang perlunya teknologi berbasis IOT.
PERBAIKAN KEKERASAN DAN STRUKTUR MIKRO LOGAM KUNINGAN SEBAGAI BAHAN PROPELLER DENGAN METODE SHOT PEENING Margono Margono Margono; Yanti Pasmawati; Nugroho Tri Atmoko; Rizqi Ilmal Yaqin; Bambang Hari Priyambodo
Jurnal Teknologi Terapan Vol 9, No 2 (2023): Jurnal Teknologi Terapan
Publisher : P3M Politeknik Negeri Indramayu

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.31884/jtt.v9i2.431

Abstract

Brass metal is widely used as a supporting equipment material, one of which is a propeller. The propeller itself is one component of the boat that rotates and produces thrust energy. The continuous use of propellers results in degradation or a decrease in quality and service life. The degradation of the propeller is affected by the hardness, toughness, and corrosion resistance of the working environment. To improve the quality of the propeller, shot peening treatment was carried out on its surface. Shot peening is a continuous shooting process with fine particles in the form of steel balls on the surface of the object. Shot peening can increase the density of the microstructure and produce compressive residual stress which causes the surface hardness to also increase. Shot peening is carried out with variations in duration of 2, 4, 6, 8, and 10 minutes, 100 mm shooting range, and 7 Bar firing pressure. The steel ball particles used have a hardness of 40-50 HRC and a diameter of 5 mm. The results of the hardness test showed an increase in the surface hardness of the spesimens for a duration of 2, 4, 6, 8, and 10 minutes, respectively 189, 294, 302, 324, 330, dan 341 HV. The microstructure of the spesimen after shot peening looks tighter and denser. The highest hardness value is 341 HV or an increase of 80% compared to raw material.
Co-Authors Andries Anwar Atmoko, Nugroho Tri Bambang Hari Priyambodo Dewi Sartika Fero Triando Margono Margono Margono Muhammad Ariandi Nina Paramithya Noer Fadzri Perdana Dinata Rizqi Ilmal Yaqin Sulaiman Sulaiman Sunda Ariana, Sunda