Article Per Year (5 Year)
p-Index From 2019 - 2024
0
P-Index
This Author published in this journals
All Journal Jurnal Sains dan Teknologi Farmasi Jurnal Riset Kimia
Asiska Permata Dewi
Fakultas Farmasi, UniversitasAndalas
Chemistry Computer Science & IT Education

Published : 4 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 4 Documents
Search

 1 
UJI BIODEGRADASI FILEM PLASTIK CAMPURAN POLISTIREN DENGAN POLI(3 HIDROKSIBUTIRAT-KO-3-HIDROKSIVALERAT) DALAM LUMPUR Dewi, Asiska Permata; Octaviani, Melzi; Rustini, Rustini; Zaini, Erizal; Djamaan, Akmal
Jurnal Sains dan Teknologi Farmasi Vol 17, No 1 (2012)
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

An assay of biodegradation of plastic film combination of polystyrene (PS) and poli (3-hydroxy butyrate-ko-3-hydroxyvalerate) [P(3HB-ko-3HV)] has been conducted. The assay was done by using soil burial test method. The plastic film was made by blending technique of various composition of PS/P(3HB-ko-3HV) in to the mud. The remaining weight of plastic film was determined gravimentically time intervals 1,2,3,4 and 5 weeks of burial. Result showed that the P(3HB-ko-3HV) had an influence on the degradation rate of plastic film. The biodegradation rate increased with an increase in P(3HB-ko-3HV) content in the mixture. The rate was derived from linear regression equation and parameters such as biodegradation rate constant (k), t 50 % and t 95% were obtained. It was found that for combination of  PS/P(3HB-ko-3HV) 95:5 k= 1,26% b/b per week , t 50 % = 39,07 weeks and t 95 % = 74,783 week for the mixture of PS/P(3HB-ko-3HV) 90:10  k = 1,604 % b/b per week, t 50 % = 30,57 week and t 95 % = 58,62 week. For the mixture of PS/P(3HB-ko-3HV), 85:15 k = 2,663 % b/b per week, t 50 % = 17,95 week and t 95 % = 34,85 week. While those of pure PS plastic film k = 0,24 % b/b per week, t 50 % = 201,85 week and t 95 % = 354,55 week which indicated a very slow biodegradation. Analysis by SEM showed that the surface of plastic film was eroded and damaged during the burial. The amount of bacterial colony per 1 gram of mud was 2,31x107.
Kajian Biodegradasi Filem Plastik Campuran Polimer Sintetik dengan Biopolimer dalam Larutan Air Octaviani, Melzi; Dewi, Asiska Permata; Boestari, Agusri; Zaini, Erizal; Djamaan, Akmal
Jurnal Sains dan Teknologi Farmasi Vol 17 No 1 (2012)
Publisher : Fakultas Farmasi Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

A study on degradation of plastic film of the mixture of polystyrene sintetic polymers (PS) with poli(3-hidroxyibutirat) [P(3HB)] dan poli(3-hidroksibutirat-ko-3-hidroxyvalerat) [P(3HB-ko-3HV)] biopolymers in-vitro and in-vivo has been done. The assay was done by immersion test method in aquadest, river water at various pH of 4,6,8, and 10 respectively. Degradation rate was determined by linear regression with parameters including : t 50%, t 95% and rate constant (k). Degradation rate of plastic film of 1 PS/P(3HB) 95:5 at pH 6 was the fastest with k = 0,79 % week, t 50 % = 63,06 week and t 95 % = 119,84 week, followed by PS/P(3HB) 90 : 10 with k = 1,22 % / week, t 50 % = 41,25 week and t 95 % = 78,21 week and PS/P(3HB) 80 : 20 with k = 3,16 % week, t 50 % = 15,81 week and t 95 % = 30,05 week while pure PS plastic film (100 : 0 ) did not degraded at all. The degradation rate of a mixture of plastic film in river water, PS/P(3HB-ko-3HV) 95:5 showed k= 0,64 % week, t 50 % = 82,63 week and t 95 % = 157,17 week, PS/P(3HB-ko-3HV) 90:10 with k = 0,69 % week, t 50 % = 72,16 week and t 95 % = 137,4 week ; PS/P(3HB-ko-3HV) 85:15 with k = 0,74 %/week, t 50% = 66,79 week and t 95% = 127,32 week, while the pure PS plastic film (100:0) did not degrade.
Uji Biodegradasi Filem Plastik Campuran Polistiren dengan Poli(3 Hidroksibutirat-Ko-3-Hidroksivalerat) dalam Lumpur Dewi, Asiska Permata; Octaviani, Melzi; Rustini, Rustini; Zaini, Erizal; Djamaan, Akmal
Jurnal Sains dan Teknologi Farmasi Vol 17 No 1 (2012)
Publisher : Fakultas Farmasi Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

An assay of biodegradation of plastic film combination of polystyrene (PS) and poli (3-hydroxy butyrate-ko-3-hydroxyvalerate) [P(3HB-ko-3HV)] has been conducted. The assay was done by using soil burial test method. The plastic film was made by blending technique of various composition of PS/P(3HB-ko-3HV) in to the mud. The remaining weight of plastic film was determined gravimentically time intervals 1,2,3,4 and 5 weeks of burial. Result showed that the P(3HB-ko-3HV) had an influence on the degradation rate of plastic film. The biodegradation rate increased with an increase in P(3HB-ko-3HV) content in the mixture. The rate was derived from linear regression equation and parameters such as biodegradation rate constant (k), t 50 % and t 95% were obtained. It was found that for combination of  PS/P(3HB-ko-3HV) 95:5 k= 1,26% b/b per week , t 50 % = 39,07 weeks and t 95 % = 74,783 week for the mixture of PS/P(3HB-ko-3HV) 90:10  k = 1,604 % b/b per week, t 50 % = 30,57 week and t 95 % = 58,62 week. For the mixture of PS/P(3HB-ko-3HV), 85:15 k = 2,663 % b/b per week, t 50 % = 17,95 week and t 95 % = 34,85 week. While those of pure PS plastic film k = 0,24 % b/b per week, t 50 % = 201,85 week and t 95 % = 354,55 week which indicated a very slow biodegradation. Analysis by SEM showed that the surface of plastic film was eroded and damaged during the burial. The amount of bacterial colony per 1 gram of mud was 2,31x107.
MANUFACTURE OF PLASTICS FILM CONTAINING OF POLYSTIRENE, POLYCAPROLACTONE, POLY(3-HIDROKSIBUTYRATE-CO-3- HIDROXYVALERATE) AND BIODEGRADATION STUDY IN OCEAN WATER Dewi, Asiska Permata; Zaini, Erizal; Djamaan, Akmal
Jurnal Riset Kimia Vol 7, No 2 (2014): March
Publisher : Universitas Andalas

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.25077/jrk.v7i2.167

Abstract

 ABSTRACTThe manufacture of a biodegradable plastics film containing of polymer synthetic polystyrene(PS) and biopolymer of polycaprolactone (PCL), poly(3-hydroxybutyrate-co-3-hydroxyvalerate)[P(3HB-ko-3HV)] and biodegradation study in ocean water has been carried out. Plastics filmcontaining of PS/PCL/P(3HB-ko-3HV) produced by blending techniques followed by solventcasting with ratios were of 100/0/0, 95/5/0, 95/0/5, 90/5/5, 85/10/5, 85/5/10. This testing wasconducted based on immersion test method recommend by American Society for Testing andMaterials. Poly blend plastics film PS/PCL/P(3HB-ko-3HV) were characterized by tensilestrength, thermal properties and SEM analysis. The profiles of the rate biodegradation view byweight reduction of the tested plastic film for 1-7 weeks period. Tensile strength analysisshowed the decreasing of tensile strength with the addition of P(3HB-ko-3HV). Thermalanalysis showed a decreasing in the melting point with the addition of PCL and P(3HB-co-3HV). SEM micrograph showed the destruction occurred and erosion at surface of plastic filmduring observation time. The rate of biodegradation showed that increasing of PCL and P (3HBco-3HV) in a mixture of plastic film, so biodegradation increased.Keywords: polystyrene, polycaprolactone, poly(3-hidroxybutyrate-co-3-hydroxyvalerate),biodegradation, film plastic.