<![CDATA[A B S T R A C TThe objective of this research was to determine the efficiency of the creatinine transport using chitosan alginate cross linked by polyvinyl alcohol (PVA) 0.1% with 70, 100, and 130 mg/L of creatinine concentration. The subject of this study was the membranes of chitosan alginate PVA, while the object of this study was the efficiency of the creatinine transport. The PVA 0.1% cross-linking chitosan-alginate membrane (1:0.15) was successfully synthesized. The membrane synthesized was characterized by FTIR, as well as tensile and strain test. The FTIR spectra showed that there is a new peak of the amino group of chitosan and carboxyl group of alginate at ca. 1651 cm-1. The hydroxyl group appears at ca. 1088 cm-1 while ester groups at ca. 1088 cm-1 and ca. 1265 cm-1 which indicate the cross binding between alginate and PVA. The water uptake test of the chitosan alginate PVA membrane reaches 257.76% for 6 hours. The tensile test results of the membrane before and after creatinine transport are 2.77 MPa and 12.56 MPa while the strain tests yield 14.24% and 18.51%, respectively. The maximum efficiency of the creatinine transport using the chitosan-alginate cross linked by PVA is 51.02% at 130 mg/L creatinine. This creatinine transport result using the PVA cross linking chitosan-alginate membrane are more efficient than chitosan-pectin membrane (25.24%) with the same creatinine concentration.Keywords: chitosan-alginate PVA membrane; creatinine; cross-link; synthesis; transportA B S T R A KPenelitian ini bertujuan untuk menentukan nilai efisiensi transpor kreatinin menggunakan membran kitosan-alginat tertaut silang polivinil alkohol (PVA) 0,1% dengan konsentrasi kreatinin 70, 100 dan 130 mg/L. Subjek dalam penelitian ini adalah membran kitosan-alginat PVA, sedangkan objek penelitian ini adalah pengaruh efisiensi transpor pada variasi konsentrasi kreatinin. Membran kitosan alginat (1:0,15) tertaut silang PVA 0,1% telah berhasil disintesis. Karakterisasi membran kitosan-alginat tertaut silang PVA diperoleh untuk spektra FTIR membran menunjukkan bahwa telah terjadi pergeseran serapan gugus amino dari kitosan dan gugus karboksil dari alginat pada puncak sekitar 1651 cm-1. Pada bilangan gelombang 3363,86 cm-1 terdapat serapan gugus –OH serta pada bilangan gelombang sekitar 1088 cm-1 dan 1265 cm-1 berasal dari gugus ester yang menunjukkan ikatan silang antara alginat dan PVA. Hasil uji serapan air pada membran kitosan-alginat PVA selama 6 jam mencapai rata-rata 257,76%. Hasil uji tarik membran sebelum dan setelah transpor masing-masing: 2,77 MPa dan 12,56 MPa dan untuk hasil uji regang membran sebelum dan setelah transpor masing-masing: 14,24% dan 18,51%. Efisiensi transpor kreatinin pada membran kitosan-alginat tertaut silang PVA mencapai efisiensi transpor maksimal pada konsentrasi 130 mg/L (51,02%). Efisiensi transpor kreatinin ini lebih tinggi jika dibandingkan menggunakan membran kitosan-pektin (25,24%) pada konsentrasi yang sama.Kata kunci: kreatinin; membran kitosan-alginat PVA; sintesis; taut silang; transpor]]>
Copyrights © 2018