<![CDATA[Admixture is an additional ingredient in concrete that is added when mixing concrete takes place in the hope of changing the properties of concrete to make it more suitable for a particular job. In this study, the material used was Sikacrete W with a percentage of 0%, 13% and 16% by weight of cement. The specimens used were cylinders (15 x 30) cm of 12 specimens for each FAS. FAS variations in this study included 0.35, 0.40 and 0.50 with a test age of 28 days. The results of this study, for FAS 0.35 the average concrete compressive strength for STATPLA was 280.24 kg/cm2, STATPDA was 110.38 kg/cm2, SDATPDA (13%) was 244.00 kg/cm2 and SDATPDA (16%) was 256.89 kg/cm2. FAS 0.40 average concrete compressive strength for STATPLA is 272.09 kg/cm2, STATPDA is 94.37 kg/cm2, SDATPDA (13%) was 237.18 kg/cm2 and SDATPDA (16%) was 249.18 kg/cm2. FAS 0.50 average concrete compressive strength for STATPLA was 238.83 kg/cm2, STATPDA was 74.05 kg/cm2, SDATPDA (13%) was 192.22 kg/cm2 and SDATPDA (16%) was 202.23 kg/cm2. These results indicate that there is an influence on FAS variations in concrete casting in brackish water with the addition of admixture.]]>
Copyrights © 2023