Article Per Year (5 Year)
p-Index From 2019 - 2024
0
P-Index
This Author published in this journals
All Journal Jurnal Riset Industri Jurnal Dinamika Penelitian Industri Agrin : Jurnal Penelitian Pertanian
Popy Marlina, Popy
Balai Riset dan Standardisasi Industri Palembang
Agriculture, Biological Sciences & Forestry Industrial & Manufacturing Engineering

Published : 9 Documents Claim Missing Document
Claim Missing Document
Check
Articles

Found 1 Documents
Search
Journal : Agrin : Jurnal Penelitian Pertanian

 1 
PERUBAHAN KEKERASAN KOMPON KARET DENGAN BAHAN PENGISI ARANG AKTIF TEMPURUNG KELAPA DAN NANO SILIKA SEKAM PADI Marlina, Popy; Pratama, Filli; Hamzah, Basuni; Pambayun, Rindit
Agrin : Jurnal Penelitian Pertanian Vol 18, No 1 (2014): Agrin
Publisher : Jenderal Soedirman University

Show Abstract | Download Original | Original Source | Check in Google Scholar | DOI: 10.20884/1.agrin.2014.18.1.214

Abstract

Produk karet sering mengalami kerusakan, terutama terjadinya pengerasan pada saat penyimpanan, pengangkutan dan penggunaannya.  Tujuan penelitian ini untuk mengetahui perubahan mutu kompon karet setelah pengusangan.  Perlakuan kompon karet yang digunakan dalam penelitian ini adalah arang aktif tempurung kelapa 10 phr dan nano silika sekam padi 40 phr) dan metode yang digunakan adalah metode akselerasi.  Variasi perlakuan yang diteliti dalam pengukuran umur simpan adalah suhu penyimpanan (60 oC, 70 oC dan 80 oC) dan lama penyimpanan (1, 2, 3, 4, 5, 6 dan 7 hari).  Parameter mutu yang digunakan untuk menentukan keberterimaan produk adalah nilai kekerasan kompon karet.  Peningkatan kekerasan kompon karet pada suhu penyimpanan  60oC dengan kisaran nilai kekerasan sebesar 53-56 Shore A, suhu 70oC kisaran nilai kekerasan 53-57 Shore A dan 80oC kisaran nilai kekerasan 53-59 Shore A. Kata kunc : kompon karet,  arang aktif tempurung kelapa, nano silika sekam padi ABSTRACTThe rubbery products are easily hardened during storage, transportation and usage.  The objective of the research was to  study changes in quality. Treatment of rubber compound used in this study is coconut shell activated charcoal and nano silica 10 phr 40 phr rice husk).  Variation in the observed treatment measurements ageing is storage temperature (60oC, 70oC and 80oC) and storage time (1, 2, 3, 4, 5, 6 and 7 days).  Quality parameters used to determine the acceptability of the product is the value of hardness rubber compound. Increased hardness rubber compound at 60 ° C with a storage temperature range of values of 53-56 Shore A hardness, 70 ° C range of 53-57 Shore A hardness values and hardness value of 80 ° C range 53-59 Shore A. Key words : Rubber compound, coconut shell activated charcoal and rice husk silica nano