Magnetoresistansi Divais Spintronika TiO2:Co/Si/TiO2:Co [Spintronics Magnetoresistance Device with TiO2:Co/Si/TiO2:Co] Edy Supriyanto; Agus Subagio; Hery Sutanto; Horasdia Saragih; Maman Budiman; Pepen Arifin; Sukirno Sukirno; Mohamad Barmawi
Jurnal Matematika & Sains Vol 12, No 1 (2007)
Publisher : Institut Teknologi Bandung

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

TiO2:Co thin films were grown on Si substrates by Metalorganic Chemical Vapor Deposition (MOCVD) technique using titanium(IV)isopropoxide and tris(2,2,6,6-tetramethyl-3,5-heptanedionato)cobalt (III), and oxygen gas. The films grown at temperature of 450 oC were crystalline having a rutile structure with (002) orientation. Based on Energy Dispersive Spectroscope (EDS) analysis, Co content in TiO2 was 1.83% and films exhibit ferromagnetic properties at room temperature. Hysteresis curves obtained from Vibrating Sample Magnetometer (VSM) measurement have coercive and saturation magnetic fields of 130 Oe and 2.1 emu/cm3, respectively. Application of TiO2:Co as injection material in spintronic device with TiO2:Co/Si/TiO2:Co structure was investigated. The effect of polarized spin injection (magnetoresistance phenomenon) was observed from the current-voltage characteristics of the device.
Pengaruh Temperatur Penumbuhan terhadap Struktur Kristal dan Morfologi Film Tipis TiO2:Eu yang Ditumbuhkan dengan Metode MOCVD [The Effect of Growth Temperature on the Crystall Structure and Morphology of the Thin Film TiO2:Eu Grown with MOCVD Method] Edy Supriyanto; Goib Wiranto; Hery Sutanto; Agus Subagio; Mikrajuddin Abdullah; Maman Budiman; Pepen Arifin; Sukirno Sukirno; Mohamad Barmawi
Jurnal Matematika & Sains Vol 12, No 2 (2007)
Publisher : Institut Teknologi Bandung

Show Abstract | Download Original | Original Source | Check in Google Scholar

Abstract

Thin film of TiO2:Eu had been grown on an n-type Si(100) substrate using Metalorganic Chemical Vapor Deposition (MOCVD) method with titanium (IV) isopropoxide [Ti{OCH(CH3)2}4] 99.99% and europium nitrate [Eu(NO3)3.6H2O] 99.99% as the metal organic precursors. The tetrahydrofuran (THF) was used as a solvent for the precursor. X-ray Diffraction (XRD) analysis showed that the TiO2:Eu thin film grown at temperature of 450 οC had crystal planes of rutile (200), rutile (002) and anatase (211), whereas film grown at 500 οC resulted in a crystal plane of rutile (002) with columnar grain and surface morphology relatively smooth. On the other hand, film grown at temperature of 550 οC has rutile (200) and rutile (002) planes. The surface morphology of thin films TiO2:Eu was affected by Eu atom concentration. The roughness of surface morphology increased with increasing Eu content and therefore the grains became larger. It can be concluded that the crystal structure and surface morphology properties of the films depended significantly on the substrate temperature.